Ionic conductivity of Ga-doped LLZO prepared using Couette?Taylor reactor for all-solid lithium batteries
Ionic conductivity of Ga-doped LLZO prepared using Couette?Taylor reactor for all-solid lithium batteries

양승훈  김민영  김다혜  정하영  류혜민  한종훈  이무성  김호성 
  • 초록

    A Couette?Taylor reactor and a batch reactor were used to synthesize garnet-related LLZO materials (Li7-3xMxLa3Zr2O12, M = Ga, Al) for all-solid batteries, and the properties of the resulting samples werecompared. Ga-doped LLZO synthesized with the Couette?Taylor reactor comprised cubic phase primarynanoparticles; the calculated lattice parameter and crystallite size for the Couette?Taylor and batchreactor samples were a = 12.98043 A and 129.8 nm and a = 12.97568 A and 394.5 nm, respectively. Theparameters for the Al-doped LLZO congener synthesized with the Couette?Taylor reactor werea = 13.10758 A, c = 12.67279 A, and 132.5 nm. The cross-section of the Ga-doped LLZO pellet synthesizedwith the Couette?Taylor reactor showed a denser microstructure than that of the other pellets, with arelative density of 98%. The total ionic conductivity of the Ga-doped LLZO pellets synthesized with theCouette?Taylor reactor was 1.2?1.7510 3 S/cm at 25 C. This value contrasts sharply with that of thesample from the batch reactor (3.9 10 4 S/cm). This is may be related to the large size of Ga doped intothe LLZO crystallite structure and the primary nanoparticles, which promoted sintering of the pellet.


 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.
유료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.