금속 구조 변화에 따른 선택 화학기상증착 W Plug의 접합 신뢰성 연구
The Effects of Metal Structure on the Junction Stability of Sub-micron Contacts Using Selective CVD-W Plug

최경근    (현대전자㈜반도체 연구소   ); 김춘환    (현대전자㈜반도체 연구소   ); 박흥락    (현대전자㈜반도체 연구소   ); 고철기    (현대전자㈜반도체 연구소  );
  • 초록

    The junction failure mechanism of W plugs has not been fully understood while the selective W deposition has been widely used for plugging interconnection lines. In this paper, the thermal stability and junction failure mechanism of sub-micron contacts using selective CVD-W plugs were intensively studied with the metal lines of AISiCu, Ti/AISiCu and TiN/AISiCu. The experimental results showed that the contact chain resistance and leakage current in the AISiCu and Ti/AISiCu metallizations were significantly degraded after annealing. From the SEM analysis, it was found that the junction spiking, due to the Al atoms diffusion along the porous interface between selective CVD-W and contactside wall, caused the junction failure. In constast, there was no degradation of the contact resistance and junction leakage current in TiN/AISiCu metal structu-re. It is believed that the TiN barrier layer could prevent AI(Ti) atoms Fromdiffusing. Therefore, TiN barrier between W plug and Al should be used to impro-ve the thermal stability of sub-micron contacts using the selective CVD-W plugs.


 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기