4불화탄소 플라즈마처리에 의한 폴리에스테르 직물의 발수가공
Water Repellent Finish of Polyester Fabric Using Carbontetrafluoride Plasma Treatment

모상영    (충남대학교 공과대학 섬유공학과   ); 이용운    (충남대학교 공과대학 섬유공학과   ); 김태년    (전주 우석대학 의상학과   ); 천태일    (동의대학교 생활과학대학 의류학과  );
  • 초록

    In order to produce a water repellent surface on polyester fabric, samples were treated in the atmosphere of $CF_4$ glow discharge plasma. The samples used in the study were ployester fabric and poyester film. The purpose of film treatment is for the comparison of hydrophobicity with fabric sample at same treatment condition. Radio frequency(13.56MHz) generator was used as electric source and its in put power is 100 Watt. Water repellency was evaluated by contact angle measurement. Result obtained are as follows. 1) Fiber interstice of original fabric was ana lysed as 0.43 $\mu$ m, and this value was sufficiently ideal for making water repellent fabric. 2) The most favorable setting position of substrate was the center area between two electrodes. 3) Fabric contact angle was higher than film contact angle at same treatment condition, and its difference was more than 50 ${\circ}$ . And it was incapalbe of fabric contact angle measurement when the film contact angle was less than 90 ${\circ}$ . because the fabric is susceptible to absorption of water by the capillary effect. 4) Fabric contact angle can not revealed the precise defferences of surface hydrophobicity, however, the film contact angle showed the real hydrophobic nature. 5) It was not sufficient method to evaluate the hydrophobicity of fabric surface by merely measure of the water contact angle. 6) It showed high water repellent nature at 0.06 torr of $CF_4$ plasma gas pressure and duration of 45 seconds treatment, and it can not be anticipated more improved nature if the pressure and duration of treatment time were increased.


 저자의 다른 논문

  • 모상영 (7)

    1. 1983 "저온 플라즈머를 이용한 섬유고분자재료의 표면개질" 韓國纖維工學會誌 = Textile science and engineering 20 (1): 57~70    
    2. 1983 "Plasma Graft중합에 의한 Poly(ethylene Terephthalate) 섬유의 표면개질에 관한 연구" 韓國纖維工學會誌 = Textile science and engineering 20 (3): 1~13    
    3. 1984 "Nylon 6 섬유의 습윤성에 관한 연구" 韓國纖維工學會誌 = Textile science and engineering 21 (6): 51~57    
    4. 1987 "플라즈마를 이용한 폴리에틸렌테레프탈레이트의 친수 그라프팅" 韓國纖維工學會誌 = Textile science and engineering 24 (3): 80~86    
    5. 1987 "페놀 수지를 매트릭스로한 무기섬유 복합재료의 융삭 현상" 韓國纖維工學會誌 = Textile science and engineering 24 (5): 14~22    
    6. 1989 "저온 Plasma를 이용한 Poly(ethylene terephthalate)에의 Acrylic Acid의 기상 Graft 공중합 반응(I)" 韓國染色加工學會誌 = Textile coloration and finishing 1 (1): 7~18    
    7. 1999 "플루오르 화합물을 플라즈마 처리한 PET 직물의 표면특성" 韓國染色加工學會誌 = Textile coloration and finishing 11 (1): 25~33    
  • 천태일 (18)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 이용한 콘텐츠
이 논문과 함께 출판된 논문 + 더보기