요업학회지 = Journal of the Korean Ceramic Society v.32 no.12, 1995년, pp.1424 - 1432   피인용횟수: 1

적외 광투과 Chalcogenide계 유리의 제조 및 특성
Preparasion and Characterization of Chalcogenide Glass with IR-Transmittance

송순모   (연세대학교 세라믹공학과UU0000936  ); 최세영   (연세대학교 세라믹공학과UU0000936  );
  • 초록

    Chalcogenide glasses having IR (8~12 ${\mu}{\textrm}{m}$ ) transmittance were prepared and their densities, thermal and mechanical properties, IR-transmittances and chemical durabilities were determined. Glass transition temperatures (Tg) of Ge-As-Se, Ge-As-Se-Te and Ge-SE-Te system glasses were in the range of 280~3 $65^{\circ}C$ , 210~236 $^{\circ}C$ and 210~26 $0^{\circ}C$ , respectively. Crystallization temperature (Tc) of Ge-Se-Te system glass was in the range of 305~40 $0^{\circ}C$ . Their thermal expansion coefficients( $\alpha$ ) were in the range of 11.7~15.2 $\times$ 10-6/K, 15.4~16.0 $\times$ 10-6/K and 17.4~27.8 $\times$ 10-6/K, respectively. Their MOR, hardness and fracture toughness were in the range of 15.2~18.6MPa, 36.1~58.2Kg/ $\textrm{mm}^2$ , 1.0~1.3 MPa.mm1/2, 18.9~24.9 MPa, 40.9~65.1Kg/ $\textrm{mm}^2$ , 1.3~1.5 MPa.mm1/2, and 24.1~30.8 MPa, 40.9~86.0Kg/ $\textrm{mm}^2$ , 1.4~1.8 MPa.mm1/2, respectively. IR transmittance of Ge-Se-Te system glass was about 60%. Ge-O extrinsic absorption peaks at 8, 12 ${\mu}{\textrm}{m}$ were significantly eliminated by the addition of Mg. Chemical durabilities in deionizied water of Ge-Se-Te system glass were good and IR-transmittances decreased with leaching time and temperature.


  • 주제어

    Chalcogenide glasses .   IR-transmittance .   Glass transition temperature(Tg) .   Crystallization temperature(Tc) .   Thermal expansion coefficient ( $\alpha$) .   MOR .   Hardness .   Fracture toughness.  

  • 참고문헌 (18)

    1. D.W. Richerson , Modern Ceramic Engineering / v.,pp.87,
    2. Modified Preparation Procedure for Laboratory Melting of Multicomponent Chalcogenide Glasses , A.M. Reitter;A.N. Sreeram;A.K. Varshneya;D.R. Swiler , J. Non-Cryst. Sol. / v.139,pp.121-128,
    3. Oxide Impurity Absorptions in Ge-Se-Te Glass Fibres , J. Nishii;T. Yamashita;T. Yamagishi , J. Mater. Sci. / v.24,pp.4293-4297,
    4. D.C. Harris , Infrared Window and Dome Materials / v.,pp.84-104,
    5. Infra-Red Transmitting Glass-Ceramics of the As-Ge-Se System Nucleated by Zirconium Selenide , J. Cheng;G. Tilloca;J Zazycki , J. Mater. Sci. / v.16,pp.2531-2543,
    6. Paramagnetic Radiation Defects in Chalocogenide Glasses and Glassy Se , I.V Chepeleva , J. Non-Cryst. Sol. / v.97,98,pp.1179-1182,
    7. Infrared Optical Glasses for Applications in 8~12 um Thermal Imaging System , J.A. Savage;P.J. Webber;A.N. Pitt , Appl. Optics / v.16,pp.2938-2941,
    8. J.A. Savage , Infrared Optical Materials and their Antireflection Coatings / v.,pp.58-118,
    9. The Glass Forming Region in and some Thermal and Infrared Transmittance Properties of Glasses of the Ge-Se-Te-Tl System , J. Nishii;Y. Kaite;T. Yamagishi , Phys. Chem. Glass / v.28,pp.55-58,
    10. Some Physical Properties of Ge-As-Se Infrared Optical Glasses , P.J. Webber;J.A. Savage , J. Non-Cryst. Sol. / v.20,pp.271-283,
    11. E. Hecht , Optics / v.,pp.552-555,
    12. Relaxation Phenomean in Amorphous Selenium Tellurium Alloys , G.C. Das.;M.B. Bever.;D.R. Uhlmann.;S.C. Moss , J. Non-Cryst. Sol / v.7,pp.251-270,
    13. R.K. Charles , Strength of Inorganic Glass / v.,pp.389-453,
    14. Mechanism of Controlled Crystallization of As-Se-Ge Glasses Nucleated by Different Nucleants , C. Jijian , J. Non-Cryst. Sol. / v.52,pp.249-262,
    15. Optical and Themal Properties of Chalcogenide Ge-As-Se-Te Glasses , T. Inagawa;R. Iizuka;T. Yamagishi;R. Yokota , J. Non-Cryst. Sol. / v.95-96,pp.801-808,
    16. Studies on Some Ge-Se-Te Glasses , S. Mahadevan;A. Giridhar;A. K. Singh , J. Non-Cryst. Sol / v.103,pp.179-194,
    17. R.W. Cahn;P. Haasen;E.J. Kramer , Materials Science and Technology / v.9,pp.381-391;441-442,
    18. Glass Formation in the Chalcogenide System Se-Ge-As , G.H. Frischat , Proc SPIE / v.400,pp.73-77,
  • 이 논문을 인용한 문헌 (1)

    1. 1996. "Controlled Crystallization and its Effects on Some Properties of Ge-Se-Te Chalcogenide Glass" 요업학회지 = Journal of the Korean Ceramic Society, 33(8): 855~862     

 저자의 다른 논문

  • 최세영 (43)

    1. 1976 "오지그릇용 무연생유에 관한 연구" 요업학회지 = Journal of the Korean Ceramic Society 13 (2): 17~23    
    2. 1992 "기체분리용 세라믹 복합분리막의 개발: II. 극미세 입자 $TiO_2$ 졸의 제조 및 코팅 특성" 요업학회지 = Journal of the Korean Ceramic Society 29 (9): 739~749    
    3. 1993 "Na-Ca-Si-O-N계 Oxynitride Glass의 제조 및 특성" 요업학회지 = Journal of the Korean Ceramic Society 30 (2): 85~92    
    4. 1993 "Sol-Gel법에 의한 $TiO_2-SiO_2$계 저반사 박막의 제조 및 특성" 요업학회지 = Journal of the Korean Ceramic Society 30 (9): 775~783    
    5. 1994 "Fe_2O_3-CaO-SiO_2$계 결정화 유리의 제조 및 특성(I)" 요업학회지 = Journal of the Korean Ceramic Society 31 (6): 629~636    
    6. 1994 "졸겔법에 의한 알루미나 박막의 제조 및 특성(II);코팅용 알루미나 졸의 합성 및 박막 제조" 요업학회지 = Journal of the Korean Ceramic Society 31 (8): 911~919    
    7. 1994 "$CaO-TiO_2-P_2O_5$계 다공질 결정화 유리의 물성에 미치는 알카리 금속 산화물의 첨가효과" 요업학회지 = Journal of the Korean Ceramic Society 31 (11): 1337~1345    
    8. 1995 "졸겔법에 의한 알루미나 박막의 제조 및 특성 (III) 저반사 코팅유리의 제조" 요업학회지 = Journal of the Korean Ceramic Society 32 (1): 57~62    
    9. 1995 "분상법을 이용한 봉규산염계 다공질 유리의 제조 및 특성;$ZrO_2$와 MgO 첨가 영향" 요업학회지 = Journal of the Korean Ceramic Society 32 (3): 385~393    
    10. 1995 "용융법에 의한 수용성 유리의 제조 및 특성 (I) : 용해 특성, 살균 효과 및 세포 독성" 요업학회지 = Journal of the Korean Ceramic Society 32 (10): 1093~1102    

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
  • 한국세라믹학회 : 저널
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기