오버레이 용접법에 의한 Al-Cu 합금 경화후막의 특성
A Characteristics of Thick and Hard Al-Cu Alloy by Overlaying Welding Process

박정식    (대구보건전문대학, 용접공업과   ); 양변모    (경북대학교 금속공학과   ); 박경재    (경북대학교 금속공학과  );
  • 초록

    It was attempted to improve the wear resistance of Al alloy under the load condition by making a formation of the thicker surface hardening alloy layers. The thicker surface hardening alloy layers were formed on 6061 Al alloys overlayed by MIG and TIG welding process with Cu powders feeding. The characteristics of hardening and wear resistance have been investigated in relation to the microstructures of alloyed layers, with a selection of optimum alloying conditions for formation of overlaying layer. The results obtained were summarized as follows With increasing feeding rate of Cu powders by MIG welding, the hardness and specific wear of the overlay weld alloys were increased. It is considered that these high hardness and specific wear of overlay weld alloys were due to the formation of Θ( $Al_2Cu$ ) phases. With increasing feeding rate of Cu powders by TIG welding, the hardness and specific wear of the overlay weld alloys were increased in feeding rates 12 and 18g/min. However, the hardness and specific wear were decreased in the powder feeding rate 38g/min. It is considered that considered that decrease of hardness and specific wear in the powder feeding rate 38g/min due to formation of ${\gamma}$ ( $Al_4Cu_9$ ) phases.


  • 주제어

    알루미늄 합금 .   표면경화 .   오버레이, 살붙이기 .   불활성가스 금속아크용접 .   불활성가스 텅스텐아크용접 .   Aluminum Alloy .   Surface Hardining .   Overlaying .   MIG Welding .   TIG Welding.  

  • 참고문헌 (15)

    1. アルミニウム合金の溶接(鐵道車兩) , 寺本福彦 , 日本溶接學會誌 / v.53,pp.124-127,
    2. 航空エンジン部品へのレ-ザ肉盛溶接の適用 , 森田昭彦 , 溶接技術 / v.39,pp.74-78,
    3. エンジン部品へのレ-ザ肉盛溶接の適用 , 中田建二;町田洋一;牙田雅己;鳥居勳;中川政宏;森和彦 , 溶接技術 / v.39,pp.68-73,
    4. 電子ビ-ム による表面改質 , 丸山敏郞;大田正雄 , 溶接技術 / v.38,pp.75-81,
    5. アルミニウム合金の表面厚膜硬化技術の現狀 , 松田福久 , 溶接技術 / v.39,pp.72-76,
    6. 複合化による新機能材料の創造 , 北田正弘 , 日本金屬學會會報 / v.17,pp.956-958,
    7. アルミニウム合金の溶接(船舶) , 鄕肥 , 日本溶接學會誌 / v.53,pp.120-124,
    8. アルミニウム合金の溶接(航空機) , 永井裕善 , 日本溶接學會誌 / v.53,pp.162-167,
    9. アルミニウム合金の溶接 , 內田彰 , 日本溶接學會誌 / v.38,pp.955-969,
    10. アルミニウム表面厚膜硬化技術の現狀と可能性 , 松田福久 , 日本輕金屬 / v.40,pp.746-752,
    11. 粉體接合.加工技術の現狀 , 新成夫 , 溶接技術 / v.39,pp.97-103,
    12. Microstructure and Tribological Behavior of Al-Si Alloy , S. Das , The 3rd International Conference on Aluminum Alloys / v.,pp.503-508,
    13. アルミニウム合金のための表面改質 , 成願茂利;佃市三 , 溶接技術 / v.38,pp.77-83,
    14. プラズマ粉體肉盛溶接によるアルミニウムの表面複合合金化 , 松田福久;中田一博;靑水茂樹;永井建介 , 溶接技術 / v.38,pp.82-86,
    15. The Effect of Dispersoids on the Recrystallisation Behavior of a Series of Aluminum-magnesium-Silicon Alloys , S. I. Hulley;G. W. Lorimer , The 3rd International Conference on Aluminum Alloys / v.,pp.361-366,

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
  • 대한용접접합학회 : 저널
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기