사출성형한 M3/2계 고속도공구강 분말의 탄소함량 및 소결밀도 변화
Variations in Carbon Content and Sintered Density of M3/2 Grade High Speed Steel Powders on Metal Injection Molding Process

이광희    (동아대학교 공과대학 금속공학과  );
  • 초록

    An investigation was performed to apply the M3/2 grade high speed steel for metal injection molding using both prealloyed and elementally blended powders. The injected samples were subjected to a debinding step in $H_2/N_2$ gas atmosphere at a ratio that affected the carbon content of the material. The carbon content ranged from 1.4wt.% to 1.43wt%. with increasing $H_2$ content up to 80% $H_2$ in $H_2/N_2$ atmosphere for the prealloyed powders. The carbon contents of the elementally blended powders exhibited 1.44wt.% and 1.62wt.% at 10% $H_2/N_2$ and 20% $H_2/N_2$ gas, respectively. This level decreased to 0.17wt.% upon increasing the $H_2$ content. The sintered density of both powders increased rapidly as the temperature reached the liquid phase forming temperature. After forming the liquid phase, the density rapidly increased to the optimum sintering temperature for the prealloyed powders, whereas the density of mixed elemental powders goes up slowly to the optimum sintering temperature. The optimum sintering temperature and density are 126 $0^{\circ}C$ and 97.3% for the prealloyed powders and 128 $0^{\circ}C$ and 96.9% for the elementally blended powders, respectively. The microstructure of the specimen at the optimum sintering temperature consisted of fine grains with primary carbides of MC and $M_6C$ type for the prealloyed powders. The elementally blended powders exhibited coarse grains with eutectic carbides of MC, $M_2C$ and $M_6C$ type.


  • 참고문헌 (21)

    1. F. A. Kirk , Powder metallurgy / v.2,pp.70,
    2. 정형식;김병기;김용진 , 대한금속학회회보 / v.6,pp.166,
    3. G. Hoyle , High Speed Steel / v.,pp.127,
    4. R. M. German , Int. J. of P/M 1 / v.,pp.35,
    5. R. M. German , Powder Injection Molding / v.,pp.89,
    6. 구광덕;강창룡;정은;박성훈;성장현 , 분말야금학회지 / v.3,pp.50,
    7. C. S. Wright;B. Oger , Powder metallurgy / v.36,pp.213,
    8. C. S. Wright , Powder metallurgy / v.32,pp.114,
    9. P. A. Willenrment;R. A. Pett;T. J. Whalen , Bull. Amer. Ceramic Soc. / v.57,pp.744,
    10. 정형식;김용진 , 대한금속학회 제3회 분말야금 심포지엄 / v.,pp.118,
    11. Pradipt K. Kar;Bhaskar P. Saha;Gopals Upodhyaya , Int. J. of P/M, 29 / v.2,pp.393,
    12. 구광덕;이석희;김영주;정은;김영삼;성장현 , 대한금속학회지 / v.31,pp.975,
    13. R. M. German , Int. J. of P/M 1 / v.,pp.23,
    14. P. Crook;R. D. Rivers;H. J. Klein , Industrial Heating / v.54,pp.12-15,
    15. D. J. Blickwede;Ninth(Ed.) , Metal Handbook / v.,pp.784,
    16. R. Billet , J. of P/M & P/T / v.21,pp.119,
    17. K. M. Kulkami , Powder Merallurgy / v.,pp.253,
    18. M. A. Phillips , Int. J. Powder Met. / v.29,pp.15,
    19. 양형도;주동원;김순호;정은;성장현 , 대한금속학회지 / v.30,pp.1577,
    20. 三浦 秀士 , 日本金屬學會會報 / v.31,pp.711,
    21. 이구현;변응선;남기양 , 고속도강 열처리 / v.,pp.250,
  • 이 논문을 인용한 문헌 (1)

    1. Ahn, Jin-Hwan ; Heo, Jong-Seo ; Joo, Dong-Won ; Jung, Eun ; Sung, Jang-Hyun 1998. "Effect of Sintering Atmosphere and Carbon Addition on Sintered Density of M3/2 Grade High Speed Steel Powder" 한국분말야금학회지 = Journal of Korean powder metallurgy institute, 5(4): 265~272     

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 이용한 콘텐츠
이 논문과 함께 출판된 논문 + 더보기