반응소결법 및 통전가압소결법에 의한 $Ti_5Si_3$계 금속간화합물의 합성 및 치밀화
Synthesis and Densification of $Ti_5Si_3$-base Intermetallic Compounds by Reactive Sintering and Electro-Pressure Sintering

유호준    (인하대학교 공과대학 금속공학과  );
  • 초록

    $Ti_5Si_3$ intermetallics containing 0-6 wt% of Cu were made by reactive sintering (RS) under vacuum using elemental powder mixtures (Process 1), electro-pressure sintering (EPS) using RS'ed materials (Process2), and EPS using elemental powder mixtures (Process 3). Relatively low dense titanium silicides were gained by process 1, in which porosity decreased with increasing Cu content. For example, porosity changed from 42 to 19.4% with the increase in Cu content from 0 to 6 wt%, indicating that Cu is a useful sintering aid. The titanium silicides fabricated by Process 2 had a higher density than those by Process 1 at given composition, and porosity decreased with increasing Cu content. For example, porosity decreased from 38 to 6.8% with the change in Cu content from 0 to 6 wt%. A high dense titanium silicides were obtained by Process 3. In this Process, porosity decreased a little by Cu addition, and was almost insensitive to Cu content. Namely, about 9 or 7% of porosity was shown in 0 or 1-6 wt% Cu containing silicides, respectively. The hardeness increased by Cu addition, and was not changed markedly with Cu content for the silicides fabricated by Process 3. This tendency was considered to be resulted from porosity, hardening of grain interior by Cu addition, and softening of grain boundary by Cu-base segregates. All these results suggested that EPS using elemental powder mixtures (Process 3) is an effective processing method to achieve satisfactorily dense titanium silicides.


  • 참고문헌 (11)

    1. A. J. Thom;Y. M. Kim;M. Akinc , Mater. Res. Soc. Symp. Proc. / v.288,pp.1037,
    2. P. J. Meschter;D. S. Schwartz , JOM / v.11,pp.52,
    3. G. Frommeyer;R. Rosenkranz;C. Ludeke , Z. Metallkde. / v.81,pp.307,
    4. Y. Murata;Y. Higuchi;Y. Takcda;M. Morinaga;N. Yukawa , Proc. Inter. Symp. on Intermetallic Compounds(JIMIS-6) / v.,pp.627,
    5. C. T. Liu;E. H. Lee;T. J. Henson , Rep. ORNL. No. 6435 / v.,pp.,
    6. A. J. Thom;M. K. Meyer;Y. M. Kim;M. Akinc , Processing and Fabrication of Materials Ⅲ, TMS / v.,pp.,
    7. K. Pischang;E. Friedrick , Sintering Advanced in Powder Metallurgy & Paticulate Materials / v.,pp.73,
    8. R. Rosenkranz;G. Frommeyer;W. Smarsly , Mater. Sci. Eng. / v.A152,pp.288,
    9. D. M. Shah;D. Berczik;D. L. Anton;R. Hch , Mater. Sci. Eng. / v.A155,pp.45,
    10. 박경재;황선근 , 대한금속학회지 / v.34,pp.396,
    11. J. J. Nickl;H. Sprenger , Z. Metallkde. / v.60,pp.136,

 저자의 다른 논문

  • 유호준 (2)

    1. 1999 "모형헬기를 이용한 불확정 다변수 이상검출법의 응용" 전기학회논문지. The transactions of the Korean Institute of Electrical Engineers. A / A, 전력기술부문 48 (2): 136~144    
    2. 1999 "불확정 시스템에서의 복합성 이상검출 및 격리" 전기학회논문지. The transactions of the Korean Institute of Electrical Engineers. A / A, 전력기술부문 48 (3): 257~262    

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기