분말 충전 성형법을 이용한 SiC-Al Alloy 복합체의 제조
Preparation of SiC-Al alloy Composite by Pressureless Powder Packing Forming Method

박정현    (연세대학교 세라믹공학과   ); 송준광    (연세대학교 세라믹공학과   ); 백승수    (연세대학교 세라믹공학과   ); 염강섭    (연세대학교 세라믹공학과   ); 강민수    (연세대학교 세라믹공학과  );
  • 초록

    To fabricate the ceramic/metal(SiC/ Al alloy) composite, SiC preform was prepared by Pressureless Powder Packing Forming Method and 6061 Al alloy was infiltrated into the preform. Uniform compact having an average pore size of 10 ${\mu}{\textrm}{m}$ and narrow pore size distribution was prepared. Phenolic resin solution(40 wt%) was penetrated into the SiC compact, and then the compact was preheated at the temperature of 120 $0^{\circ}C$ . The pore size distribution and the microstructure of the preform were not changed by preheating. An uniform microstructure without any crack in the preform was obtained in SiC-Al alloy composite. The infiltration of 6061. Al alloy into the preform began at the temperature of 130 $0^{\circ}C$ and the amount of infiltration increased in proportion to the infiltration temperature and the soaking time. The increasement rate of the infiltration amount decreased after 3 h. As a result of the infiltration at 140 $0^{\circ}C$ for 4 h, Al alloy was well distributed in the interparticle channels and the relative density of the composite was above 98%. The strength and the fracture toughness of the composite were 303 MPa and 21.65 MPam1/2, respectively.


  • 주제어

    Pressureless powder packing forming method .   SiC-Al alloy composite .   Molten metal infiltration.  

  • 참고문헌 (17)

    1. Particle Packing Characteritics , J.S. Reed , Principles of Ceramic Processing / v.,pp.185-199,
    2. Wettability of SiO₂and Oxidized SiC by Aluminum , V. Laurent;D. Chatain;N. Eustathopoulos , Mater. Sci. Engin / v.A135,pp.89-94,
    3. Metal-Matrix Composites , J. Fleck;M.B. Bever(ed.) , Encyclopedia of Materials Science and Engineering / v.4,pp.2949-2955,
    4. Vibratory Compacting of Metal and Ceramic Powders , W.C. Bell;M.R. Lominac;E.G. Manning , J. Am. Ceram. Soc. / v.38,pp.396-404,
    5. The Wettability of Silicon Carbide by Liquid Aluminum: the Effect of Free Silicon in the Carbide and of Magnesium, Silicon and Copper Alloy Additions to the Aluminum , Do-Suck Han;H. Jones;H.V. Atkinson , J. Mater. Sci. / v.28,pp.2654-2658,
    6. Metal Matrix Composites-An Overview , D.J. Lloyd;D. S. Wilkinson(ed.) , Advanced Structural Material / v.,pp.1-21,
    7. Thermosetting Matrix Precursors , G. Savage , Carbon-Carbon Composites / v.,pp.117-129,
    8. Influence of Heat Treatment on the Tensile Properties and Fracture Behaviour of an Aluminum alloy-Ceramic Particle Composite , T.S. Srivatsan;J. Mattinggly , J. Mater. Sci. / v.28,pp.611-620,
    9. Stability of SiC in Molten Aluminum , D.J. Lloyd;E. Dewing;D.S. Wilkinson(ed.) , Advanced Structural Materials / v.,pp.71-77,
    10. Progress Continues in Composite Technology , G. Geiger , Ceram. Bull. / v.70,pp.212-218,
    11. 무가압 분말 충전 성형법을 이용한 알루미나 세라믹스의 제조(Ⅰ) , 박정현;이상진;성재석 , 한국요업학회지 / v.31,pp.31-38,
         
    12. Thermoplastic Matrix Precursors , G. Savage , Carbon-Carbon Composites / v.,pp.157-192,
    13. Improved Corrosion Resistance of Ceramic-Matrix Composites , P. Barron;J.G. Weinstein , Ceram. Bull. / v.70,pp.336-340,
    14. Interfacial Reaction Kinetics of Al/SiC Composite during Casting , R.Y. Lin;K. Kannikeswaran;R.Y. Lin(ed.);R.J. Arsenault(ed.) , Interfaces in Metal-Ceramics Composites / v.,pp.153-164,
    15. A Study on Carbonization of Phenol-Formaldehyde Resin Labelled with Deuterium and $^{13}C$ , Y. Yamashita;K. Ouchi , Carbon / v.,pp.1989-1994,
    16. Static and Dynamic Properties of Squeeze-Casting A375-SiC Particulate Duralcan Metal Matrix Composite , A. Bloyce;J.C. Summers , Mater. Sci. Engin. / v.A135,pp.231-236,
    17. Wetting and Interfacial Reactions in Al-Li-SiCp Metal Matrix Composites Processed by Spray Atomization and Deposition , M. Supta;I.A. Ibrahim;F.A. Mohamed;E.J. Lavcrnia , J. Mater Sci. / v.26,pp.6673-6684,

 저자의 다른 논문

  • 박정현 (59)

    1. 1980 "용융 알루미늄에 의한 점토결합 카올린 샤모트의 침식에 관한 연구" 요업학회지 = Journal of the Korean Ceramic Society 17 (4): 188~196    
    2. 1982 "SiC 질 공업용 도자기 개발에 관한 연구" 요업학회지 = Journal of the Korean Ceramic Society 19 (1): 5~12    
    3. 1982 "탄소피막 저항기용 자기소체 제조에 있어 Barite 활용에 관한 연구" 요업학회지 = Journal of the Korean Ceramic Society 19 (2): 95~100    
    4. 1982 "Al 분말의 산화에 의한 $Al_2O_3$ 소결에 관한 연구" 요업학회지 = Journal of the Korean Ceramic Society 19 (3): 179~186    
    5. 1983 "첨가된 알루미늄 분말의 산화가 알루미나 소결에 미치는 영향(I. 공기중, $1350~1550^{\cire}C$에서)" 요업학회지 = Journal of the Korean Ceramic Society 20 (1): 49~54    
    6. 1983 "Al-Kaolin 혼합물의 Mullite화 반응" 요업학회지 = Journal of the Korean Ceramic Society 20 (2): 123~128    
    7. 1984 "첨가된 알루미늄 분말의 산화가 알루미나 소결에 미치는 영향(II. 공지궁 1,600~1,80$0^{\circ}C$에서)" 요업학회지 = Journal of the Korean Ceramic Society 21 (3): 259~265    
    8. 1984 "Kaolin-Al 혼합물의 고온 Mullite 화 반응" 요업학회지 = Journal of the Korean Ceramic Society 21 (4): 327~332    
    9. 1986 "Al 분말의 점화열을 이용한 Sialon 분말 제조에 관한 연구" 요업학회지 = Journal of the Korean Ceramic Society 23 (2): 1~6    
    10. 1986 "Kyanite-Al 혼합물의 Mullite화 반응" 요업학회지 = Journal of the Korean Ceramic Society 23 (2): 7~12    
  • 염강섭 (4)

  • 강민수 (7)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
  • 한국세라믹학회 : 저널
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기