Hot-press법으로 제조된 $Y_2O_3$$Nb_2O_5$가 첨가된 정방정 ZrO2의 고온열화
High-Temperature Degradation of Hot-Pressed $t-ZrO_2$ Co-doped with $Y_2O_3$ and $Nb_2O_5$

이득용    (대림전문대학 금속재료과   ); 김대준    (KIST 세라믹스부   ); 조경식    (KIST 세라믹스부  );
  • 초록

    Tetragonal ZrO2 polycrystal (TZP), consisted of 90.24 mol% ZrO2-5.31 mol% Y2O3-4.45 mol% Nb2O5, were prepared using hot-press and mechanical properties and high-temperature degradation were investigated. The specimen, hot-pressed for 1 h at 140 $0^{\circ}C$ in Ar atmosphere, exhibited flexural strength of 1010 MPa and fracture toughness of 7.5 MPam1/2 and experienced no low-temperature degradation below 40 $0^{\circ}C$ . However, as aged for 100h at temperatures higher than 40 $0^{\circ}C$ , TZP was suffered by high-temperature degradation due to an extensive cavitation caused by the oxidation of carbon. XPS observation revealed that the carbon incorporated in TZPs during hot-pressing exists as either an ether-type CO or a carbonyl-type C=O. Despite of the high-temperature degradation of t-ZrO2 co-doped with Y2O3 and Nb2O5, its flexural strength and fracture toughness were superior to those of the commercial 3 mol% Y2O3-TZP hot-pressed under the identical condition as determined before and after the aging treatments.


  • 주제어

    Tetragonal $ZrO_1$ Polycrystal (TZP) .   High-Temperature Degradation .   Co .   $Co_2$ .   Oxidation.  

  • 참고문헌 (16)

    1. Sintering of 3mol%Y₂O₃-TZP and its fracture after ageing treatment , S. Chen;H. Lu , J. Mater. Sci. / v.23,pp.1195-1200,
    2. Effects of oxide additions on the stability of the tetragonal phase in TZP ceramics , H. Hofmann;B. Michel;L. J. Gauckler;J. Allemann;G. L. Messing(ed.);S. Hirano(ed.);H. Hausner(ed.) , Ceramic Transactions(Ceramic Powder Science Ⅲ) / v.,pp.961-970,
    3. R. C. Weast(ed.);M. J. Astle(ed.) , CRC Handbook of Chemistry and Physics(61st Ed.) / v.,pp.,
    4. Y₂O₃와Nb$_2O_5$가 첨가된 ZrO₂의 상 안정성 및 물리적 성질 , 이득용;김대준;조경식;장주웅 , 한국요업학회지 / v.34,pp.645-651,
         
    5. Phase analysis in zirconia system , R. C. Garvie;P. S. Nicholson , J. Am. Ceram. Soc. / v.55,pp.303-305,
    6. Fracture toughness determinations by indentation , A. G. Evans;E. A. Charles , J. Am. Ceram. Soc. / v.59,pp.371-372,
    7. Phase transformation of Y₂O₃and Nb₂O5 doped with tetragonal zirconia during low temperature aginig in air , D.-J.Kim;H. -J.Jung;D. -H. Cho , Solid State Ionics / v.80,pp.67-73,
    8. Average grain size in polycrystalline ceramics , M. J. Mendelson , J. Am. Ceram. Soc. / v.69,pp.519-522,
    9. Low-temperature aging of t-ZrO₂polycrystals with 3 mol%Y₂O₃ , H. Lu;S. Chen , J. Am. Ceram. Soc. / v.70,pp.537-541,
    10. Effect of dopants on zirconia stabilization-an X-ray absorption study;Ⅲ,charge-compensating dopants , P. Li;I. Chen;J. E. Penner-Hahn , J. Am. Ceram. Soc. / v.77,pp.1289-1295,
    11. The effect of ceria co-doping on chemical stability and fracture toughness of Y-TZP , M. M. R. Boutz;A. J. A. Winnubst;B. Van Langerak;R. J. M. Olde Scholtehuis;K. Kreuwel;A. J. Burggraaf , J. Mater. Sci / v.30,pp.1854-1862,
    12. Chemical shifts and optical properties of tin oxide films grown by a reactive ion assisted deposition , W. Choi;H. Jung;S. Koh , J. Vac. Sci. Technol A / v.14,pp.359-366,
    13. Influence of aging environment on low temperature degradation of tetragonal zirconia alloys , D.-J. Kim , J. Euro. Ceram. Soc. / v.17,pp.897-900,
    14. Effect of refractory oxides on the oxidation of graphite and amorphous carbon , A. Yamaguchi;S. Zhang;J. Yu , J. Am. Ceram. Soc. / v.79,pp.2509-2511,
    15. A modifield indentation toughness technique , R. F. Cook;B. R. Lawn , Comm. Am. Ceram. Soc. / v.66,pp.C200-C201,
    16. Mechanical properties of Y₂O₃-stabilized tetragonal ZrO₂polycrystals after ageing at high temperature , T. Masaki , J. Am. Ceram. Soc. / v.69,pp.519-522,

 저자의 다른 논문

  • 이득용 (54)

    1. 1997 "$Y_2O_3$$Nb_2O_5$가 첨가된 $ZrO_2$의 상 안정성 및 물리적 성질" 요업학회지 = Journal of the Korean Ceramic Society 34 (6): 645~651    
    2. 1997 "인가 전압이 Y-TZP의 저온열화에 미치는 영향" 요업학회지 = Journal of the Korean Ceramic Society 34 (12): 1254~1260    
    3. 1998 "$Y-Nb-TZP/Al_2O_3$ 복합체의 저온 상안정성 및 기계적 특성" 한국결정성장학회지 = Journal of the Korean crystal growth and crystal technology 8 (4): 634~639    
    4. 1999 "수계공정에 의한 알루미나 테이프로 제조한 세라믹 인공치관용 알루미나 유리 복합체의 기계적 물성" 요업학회지 = Journal of the Korean Ceramic Society 36 (10): 1123~1131    
    5. 1999 "HIP법으로 제조한 $(Y,Nb)-TZP/Al_2O_3$ 복합체의 기계적 특성" 요업학회지 = Journal of the Korean Ceramic Society 36 (12): 1381~1389    
    6. 2000 "${Fe_2}{O_3}$ 첨가에 따른 t-$ZrO_2$/${Al_2}{O_3}$ 복합체의 기계적 및 광학적 특성" 한국세라믹학회지 = Journal of the Korean Ceramic Society 37 (4): 354~358    
    7. 2000 "유기물 조성에 따른 알루미나 테이프의 열간 가압 거동" 한국세라믹학회지 = Journal of the Korean Ceramic Society 37 (8): 824~831    
    8. 2000 "Microstructural Behavior of Alumina Aggregate Compacts Prepared by Transient Liquid Phase Sintering" The Korean journal of ceramics 6 (1): 78~82    
    9. 2000 "t-ZrO$_2$/Al$_2$O$_3$복합체 상 안정성에 대한 Eu$_2$O$_3$첨가 효과" 한국결정성장학회지 = Journal of the Korean crystal growth and crystal technology 10 (3): 233~238    
    10. 2001 "알루미나 입도가 (Y,Nb)-TZP/${Al_2}{O_3}$ 복합체의 R-curve 거동에 미치는 영향" 한국세라믹학회지 = Journal of the Korean Ceramic Society 38 (10): 936~941    
  • 김대준 (36)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
  • 한국세라믹학회 : 저널
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기