분말시스압연법에 의해 제조된 알루미늄 분말성형체의 조직 및 기계적 성질
Microstructure and Mechanical Property of Aluminum Powder Compact by Powder-in Sheath Rolling Method

이성희   (한양대학교 금속재료공학과UU0001519  );
  • 초록

    A nitrogen gas atomized aluminum powder was consolidated by powder-in sheath rolling method. A pure aluminum tube with outer diameter of 12 mm and wall thickness of 1mm was used as a sheath. The aluminum tube filled with the aluminum powder, first, was cold-rolled to the thickness of 6mm for performing, and then consolidated by the cold rolling and/or subsequent hot rolling at 360, 460 and $560^{\circ}C$ . The aluminum powder compact fabricated by the sheath rolling showed high relative density more than 0.96 at any rolling conditions. The 0.2% proof stress increased with increasing hot rolling reduction and hot rolling temperature. Tensile strength was hardly affected by change in the hot rolling reduction, whereas it decreased with increasing hot rolling temperature. The powder compact showed the large elongation when cold rolling or hot rolling reduction was large. It was found that the sheath rolling was an effective method for consolidation of aluminum powder.


  • 주제어

    Powder-in sheath rolling .   High pure aluminum powder .   Microstructure .   Mechanical property.  

  • 참고문헌 (12)

    1. S. Shima and M. Yamada: Powder Metall., 27 (1984) 39. 
    2. W.F. Wang: Powder Metall., 38 (1995) 289. 
    3. K. Mizuuchi, Y. Okada and I. Ohnaka: Mater. Trans., JIM, 34 (1993) 703. 
    4. S. H. Hong and K. H. Chung: Mater. Sci. Eng., A194 (1995) 165. 
    5. L. R. Vaidyanath, M. G. Nicholas and D. R. Milner: Brit. Weld. J., 6 (1959) 13. 
    6. T. Tabata, S. Masaki, T. Yamaoka and T. Yabe: Trans. JSME, 49 (1983) 473. 
    7. I. J. Palmear: Light Alloys, 3rd ed., Arnold, London (1995) 91. 
    8. N. C. Kothari: Powder Metall. Int., 18 (1986) 321. 
    9. M. G. Nicholas and D. R. Milner: Brit. Weld. J., 8 (1961) 375. 
    10. R. M. German: Powder Metallurgy Science, 2nd, Metal Powder Institute Federation, Princeton, New Jersey, (1994) 312. 
    11. Y. Genma, Y. Tsunekawa, M. Okumiya and N. Mohri: Mater. Trans., JIM, 68 (1997) 232. 
    12. E. A. Bloch: Metall. Rev., 6 (1961) 193. 

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기