치주지지가 감소된 상태에서 섬유강화형 포스트로 수복한 치아의 실패양상 분석
AN ANALYSIS OF FAILURE MODE OF TEETH RESTORED WITH FIBER-REINFORCED POSTS UNDER THE CONDITION OF BONY RESORPTION

이병우   (강릉대학교 치과대학 치과보철학교실, 강릉대학교 구강과학연구소UU0000029  ); 이양진   (강릉대학교 치과대학 치과보철학교실, 강릉대학교 구강과학연구소UU0000029  ); 조리라   (강릉대학교 치과대학 치과보철학교실, 강릉대학교 구강과학연구소UU0000029  ); 박찬진   (강릉대학교 치과대학 치과보철학교실, 강릉대학교 구강과학연구소UU0000029  );
  • 초록

    Statement of problem : Fiber-reinforced posts have lower modulus of elasticity than titanium post or cast post-core. With this similar elasticity to that of dentin, fiber-reinforced posts have been known to have a tendency to reduce the risk of root fracture. However, there were few studies on the teeth restored with fiber-reinforced posts under the condition of reduced periodontal support. Purpose : The purpose of this study was to evaluate the fracture strength and failure mode of endodontically treated teeth restored with fiber-reinforced posts and titanium posts under the condition of reduced periodontal support. Material and method : Extracted human maxillary incisor roots were divided into 3 groups (group 1 carbon fiber post, group 2 : glass fiber post, and group 3 : titanium alloy post). After coronectomy and endodontic treatment, teeth were restored with each post systems and resin core according to the manufacturer's recommendation. Then, teeth with simulated periodontal ligament were embedded in the acrylic resin blocks at the level of 4 mm below the cemento-enamel junction. Each specimen was exposed to $10^5$ load cycles with average 30 N force in $36.5^{\circ}C$ water using a computer-controlled chewing simulator. Loads were applied at $45^{\circ}$ angle to the long axis of the teeth. After cyclic loading, teeth were subjected a compressive load until failure at a crosshead speed of 0.5 mm/min. Fracture strength (N) and failure mode were examined. The fracture strength was analyzed with one-way ANOVA and the Scheffe adjustment at the 95% significance level. Results and conclusion : The results were as follows. 1. There was no statistically significant difference in the mean fracture strength among the groups (P


  • 주제어

    Carbon fiber post .   Glass fiber post .   Fracture strength .   Failure mode .   Periodontal support.  

  • 참고문헌 (26)

    1. Stewardson DA. Non-metal post systems. Dent Update 2001;28:326-336 
    2. Cohen BI, Pagnillo MK, Condos S, Deutsch AS. Four different core materials measured for fracture strength in combination with five different designs of endodontic posts. J Prosthet Dent 1996;76:487-495 
    3. Sidoli GE, King PA, Setchell DJ. An in vitro evaluation of a carbon fiber-based post and core system. J Prosthet Dent 1997;78:5-9 
    4. Cormier CJ, Burns DR, Moon P. In vitro comparison of the fracture resistance and failure mode of fiber, ceramic, and conventional post systems at various stages of restoration. J Prosthodont 2001;10:26-36 
    5. Isidor F, Odman P, Brondum K. Intermittent loading of teeth restored using prefabricated carbon fiber posts. Int J Prosthodont 1996;9:131-136 
    6. Assif D, Bitenski A, Pilo R, Oren E. Effect of post design on resistance to fracture of endodontically treated teeth with complete crowns. J Prosthet Dent 1993;69:36-40 
    7. Heydecke G, Dent DM, Peters MC. The restoration of endodontically treated, single-rooted teeth with cast or direct posts and cores: a systemic review. J Prosthet Dent 2002;87:380-386 
    8. Quintas AF, Dinato JC, Bottino MA. Aesthetic posts and cores for metal-free restoration of endodontically treated teeth. Pract Periodont Aesthet Dent 2000;12:875-884 
    9. Carossa S, Lombardo S, Pera P, Corsalini M, Rastello ML, Preti G. Influence of posts and cores on light transmission through different all-ceramic crowns: spectrophotometric and clinical evaluation. Int J Prosthodont 2001;14:9-14 
    10. Stegaroiu R, Yamada H, Kasukari H, Miyakawa O. Retention and failure mode after cyclic loading in two post and core systems. J Prosthet Dent 1996;75:506-511 
    11. Heydecke G, Dent DM, Butz F, Hussein A, Strub JR. Fracture strength after dynamic loading of endodontically treated teeth restored with different post-and-core systems. J Prosthet Dent 2002;87:438-445 
    12. Akkayan B, Dent DM, Gulmez T. Resistance to fracture of endodontically treated teeth restored with different post systems. J Prosthet Dent 2002;87:431-437 
    13. Torbjorner A, Karlsson S, Syverud M. Hensten-Pettersen A. Carbon fiber reinforced root canal posts. Eur J Oral Sci 1996;104:605-611 
    14. Rosentritt M. Furer C, Behr M, Lang R, Handel G. Comparison of in vitro fracture strength of metallic and tooth-colored posts and cores. J Oral Rehabil 2000;27:595-601 
    15. Yi YJ. A study on the fracture strength of teeth restored with a carbon fiber post under cyclic loading. J Korean Acad Prosthodont 2000:38:640-648 
    16. King PA, Setchell DJ. An in vitro evaluation of a prototype CFRC prefabricated post developed for the restoration of pulpless teeth. J Oral RehabiI 1990;17:599-609 
    17. Purton DG, Love RM. Rigidity and retention of carbon fiber versus stainless steel root canal posts. Int Endod J 1996;29:262-265 
    18. Holmes DC, Diaz-Arnold AM, Leary JM. Influence of post dimension on stress distribution in dentin. J Prosthet Dent 1996;75:140-147 
    19. Martelli R. Fourth-generation intraradicular posts for the aesthetic restoration of anterior teeth. Pract Periodont Aesthet Dent 2000;12:579-584 
    20. Stockton LW, Williams PT. Retention and shear bond strength of two post systems. Oper Dent 1999;24:210-216 
    21. Butz F, Lennon AM, Heydecke G, Strub JR. Survival rates and fracture strength of endodontically treated maxillary incisors with moderate defects restored with different post-and-core systems : an in vitro study. Int J Prosthodont 2001;14:58-64 
    22. Mollersten L, Dr Odont, Lockowandt P, Linden L. A comparison of strength of five core and post-and-core systems. Quintessence Int 2002;33:140-149 
    23. Sirimai S, Riis DN, Morgano SM. An in vitro study of the fracture resistance and the incidence of vertical root fracture of pulpless teeth restored with six post-and-core systems. J Prosthet Dent 1999;81:262-269 
    24. Terry DA, Triolo Jr PT, Swift Jr EJ. Fabrication of direct fiber-reinforced posts: a structural design concept. J Esthet Restor Dent 2001;13:228-240 
    25. Martinez-Insua A. Silva LD, Rilo B, Santana U. Comparison of the fracture resistances of pulpless teeth restored with a cast post and core or carbon-fiber post with a composite core. J Prosthet Dent 1998;80:527-532 
    26. Krejci I, Reich T, Lutz F, Albertoni M. An in vitro test procedure for evaluating dental restoration systems. 1. A computer-controlled mastication simulator. Schweizer Monatsschrift f r Zahnmedizin 1990;100:953-960 

 저자의 다른 논문

  • 이병우 (1)

    1. 2003 "Implant overload 감소를 위한 교합면 형성 방법" 대한치과턱관절기능교합학회지 = Journal of Korean academy of stomatognathic function and occlusion 19 (2): 105~108    
  • 이양진 (15)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
유료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기