Fibers and polymers v.5 no.4, 2004년, pp.259 - 263   피인용횟수: 1
본 등재정보는 저널의 등재정보를 참고하여 보여주는 베타서비스로 정확한 논문의 등재여부는 등재기관에 확인하시기 바랍니다.

Acoustic Emission on Failure Analysis of Rubber-Modified Epoxy Resin

Lee Deok-Bo    (Reliability Analysis Research Center, Hanyang University  );
  • 초록

    Rubber-modified epoxy resins have been employed as adhesive and matrix materials for glass and corbon-fiber composites. The behavior of fracture around a crack tip for rubber-modified epoxy resin is investigated through the acoustic emission (AE) analysis of compact tension specimens. Damage zone and rubber particles distributed around a crack tip were observed by a polarized optical microscope and an atomic force microscope (AFM). The damage zone in front of pre-crack tip in rubber-modified specimen $(15wt\%\; rubber)$ began to form at about $13\%$ level of the fracture load and grew in size until $57\%$ load level. After that, the crack propagated in a stick-slip manner. Based on time-frequency analysis of AE signals and microscopic observation of damage zone, it was thought that AE signals with frequency bands of 0.15-0.20 MHz and 0.20­0.30 MHz were generated from cavitation in the damage zone and crack propagation, respectively.


  • 주제어

    Acoustic emission .   Time-frequecy analysis .   Fracture energy .   Damage zone .   Rubber-Modified Epoxy Resin .   Fracture Toughness .   Toughening mechanism .   Rubber Particle.  

  • 참고문헌 (19)

    1. R. A. Pearson and A. F. Yee, J. Mater. Sci., 21, 2475 (1986) 
    2. A. J. Kinloch, S. J. Shaw, D. A. Tod, and D. L. Hunston Polymer, 24, 1341 (1983) 
    3. L. T. Manzione and J. K. Gillham, J. Appl. Polym., 26, 889 (1981) 
    4. D. B. Lee, T. Ikeda, M. Todo, N. Miyazaki, and K. Takahashi, Trans. Japan Soc. Mech. Eng., 65, 25 (1998) 
    5. K. Arakawa, T. Mada, and K.Takahashi, Trans. Japan Soc. Mech. Eng., 66, 883 (2000) 
    6. R. Bagheri and R. A. Pearson, Polymer, 37,4529 (1996) 
    7. R. A. Pearson and A. F. Yee, J. Mater. Sci., 21, 3828 (1991) 
    8. H. R. Daghyani, Y. W. Mai, and J. Wu, J. Mater. Sci. Lett., 13, 1330 (1994) 
    9. T. K. Chen and Y. H. Jan, J. Mater. Sci., 21, 111 (1992) 
    10. D. B. Lee, J. Korean Fiber Soc., 39, 430 (2002) 
    11. A. S. Holik, R. P. Kambour, S. Y. Hobbs, and D. G. Fink, Microstructural Sci., 1, 357 (1979) 
    12. D. B. Lee, T. Ikeda, N. Miyazaki, and N. S. Choi, Trad. ASME J. Eng. Mat. & Tech., 124, 206 (2002) 
    13. D. B. Lee, T. Ikeda, N. Miyazaki, and N. S. Choi, J. Mater. Sci. Lett., 22, 229 (2003) 
    14. D. B. Lee, T. Ikeda, N. Miyazaki, and N. S. Choi, Eng. Frac. Mecha., 69, 1363 (2002) 
    15. D. B. Lee, J. Korean Fiber Soc., 39, 323 (2002) 
    16. A. F. Yee, D. M. Li, and X. Li, J. Mat. Sci., 28, 6392 (1993) 
    17. A. F. Yee and R. A. Pearson, J. Mater. Sci., 21, 2462 (1986) 
    18. W. D. Bascom, J. Mater. Sci., 16, 2657 (1981) 
    19. D. B. Lee, T. Ikeda, and N. Miyazaki, The Soc. Mat. Sci. (Japan), 50, 55 (2001) 
  • 이 논문을 인용한 문헌 (1)

    1. 2007. "" Fibers and polymers, 8(6): 571~578     

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기