Fibers and polymers v.5 no.4, 2004년, pp.289 - 296  
본 등재정보는 저널의 등재정보를 참고하여 보여주는 베타서비스로 정확한 논문의 등재여부는 등재기관에 확인하시기 바랍니다.

Thermal Decomposition Kinetics of Copolymers Derived from p-dioxanone, L-lactide and Poly(ethylene glycol)

Bhattarai Narayan    (Department of Advanced Organic Materials Engineering, Chonbuk National University   ); Khil Myung Seob    (Department of Textile Engineering, Chonbuk National University   ); Oh Seung Jin    (Department of Textile Engineering, Chonbuk National University   ); Kim Hak Yong    (Department of Textile Engineering, Chonbuk National University   ); Kim Kwan Woo    (Department of Bionano System Engineering, Chonbuk National University  );
  • 초록

    The kinetic parameters, including the activation energy E, the reaction order n, and the pre-exponential factor Z, of the degradation of the copolymers based on the poly(L-lactide) (PLLA) or poly(p-dioxanone-co-L-lactide) (PDO/PLLA) and diol-terminated poly(ethylene glycol) (PEG) segments have been evaluated by the single heating methods of Friedman and Freeman-Carroll. The experimental results showed that copolymers exhibited two degradation steps under nitrogen that can be ascribed to PLLA or PDO/PLLA and PEG segments, respectively. However, copolymers exhibited almost single degradation step in air. Although the values of initial decomposition temperature were scattered, copolymers showed the lower maximum weight loss rate and degradation-activation energy in air than in nitrogen whereas the higher value of temperature at the maximum rate of weight loss was observed in air.


  • 주제어

    Biodegradable .   Poly(p-dioxanone-co-L-lactide)-b-poly(ethyleneglycol) .   Thermogravimetric analysis .   Activation energy .   Friedman method .   Freeman-Carroll method.  

  • 참고문헌 (32)

    1. N. Saito, T. Okada, H. Horiuchi, N. Marakami, J. Takahashi, M. Nawata, H. Ota, K. Nozaki, and K. Takaoka, Nature Biotechnology, 19, 332 (2001) 
    2. C. M. Agrawal, D. Huang, J. P. Schmitz, and K. A. Athanasiou, Tissue Eng., 3, 345 (1997) 
    3. W. L. Chang, J. Appl. Polym. Sci., 53, 1759 (1994) 
    4. J. H. Flynn and L. A. Wall, J. Polym. Sci. B, 4, 323 (1966) 
    5. P. K. Chaterjee and C. M. Conrad, J. Polym. Sci. A-l, 6, 594 (1968) 
    6. A. W. Coats and J. P. Redfern, Nature, 201, 68 (1964) 
    7. F. D. Kopinke, M. Remmler, M. Moder, and O. Wachsen, Polym. Degd. Stab., 53, 329 (1996) 
    8. M. S. Eroglu, B. Hazer, O. Guven, and B. M. Baysal, J. Appl. Polym. Sci., 60, 2141 (1996) 
    9. L. Abate, S. Calanna, A. Pollicino, and A. Recca, Polym. Eng. Sci., 36, 1782 (1996) 
    10. E. S. Freeman and B. Carroll, J. Phys. Chem., 62, 394 (1958) 
    11. D. M. Cam and M. Marucci, Polymer, 38, 1879 (1997) 
    12. X. G. Li, M. R. Huang, G. H. Guan, and T. Sun, Polym. Int., 46, 289 (1999) 
    13. N. Bhattarai, H. Y. Kim, D. R. Kim, and S. J. Park, J. Polym. Int., 52, 6 (2003) 
    14. H. H. Horowitz and G. Metzger, Anal. Chem., 35, 1464 (1963) 
    15. M. S. Widmer, P. K. Gupta, L. C. Lu, R. K. Meszlenyi, G. R. Evans, K. Brandt, T. Savelt, A. Gurlek, C. W. Patrick, and A. G. Mikos, Biomaterials, 19, 1945 (1998) 
    16. N. Bhattarai, H. Y. Kim, and D. R. Lee, Polym. Degrad. Stab., 78, 423 (2002) 
    17. I. C. McNeil and H. A. Leiper, Polym. Degrad. Stab., 11, 267 (1985) 
    18. H. E. Kissinger, Anal. Chem., 29, 1702 (1957) 
    19. S. Han, C. Kim, and D. Kwon, Polymer, 38, 317(1997) 
    20. L. Reich, J. Polym. Sci. Polym. Lett. Ed., 2, 621 (1964) 
    21. D. W. Van Krevelen, C. Van Heerden, and F. J. Huntjens, Fuel, 30, 11 (1951) 
    22. M. Ranchandani, M. Pankaskie, and D. Robinson, J. Controlled Release, 43, 161 (1997) 
    23. E. S. Lipinsky, R. G. Sindair, and J. D. Browning, US Patent, 5,767,222 (1993) 
    24. T. C. Forschner, PCT Int Wo, 9721753 Al (1997) 
    25. S. Gogolewski and P. Mainil-Vailet, Biomaterials, 18, 251 (1997) 
    26. A. K. Mukerjee and M. J. Patri, J. Macromol. Sci. Chem., A26, 213 (1989) 
    27. H. Nishida, M. Yamashira, N. Hattori, T. Endo, and Y. Tokiwa, Polym. Degrad. Stab., 70, 485 (2000) 
    28. X. G. Li, M. R. Huang, G. H. Guan, and T. S. Angew, Macromol. Chem., 227, 69 (1995) 
    29. E. Bortel, S. Hodorowiez, and R. Lamot, Macromol. Chem., 180, 2491 (1979) 
    30. J. Scheirs, S. W. Bigger, and O. Delatycki, Eur. Polym. J., 27, 1111 (1997) 
    31. H. L. Friedman, J. Polym. Sci. C., 6, 183 (1964) 
    32. T. Ozawa, Bull. Chem. Soc. Jpn., 38, 1881 (1965) 

 저자의 다른 논문

  • 길명섭 (15)

    1. 2004 "The Effect of Molecular Weight and the Linear Velocity of Drum Surface on the Properties of Electrospun Poly(ethylene terephthalate) Nonwovens" Fibers and polymers 5 (2): 122~127    
    2. 2004 "진공 하에서 전기방사된 부직포의 특성에 대한 연구" 韓國纖維工學會誌 = Textile science and engineering 41 (6): 424~432    
    3. 2005 "계면활성제를 부가하여 전기방사한 PLGA 부직포의 습윤성 개선" 韓國纖維工學會誌 = Textile science and engineering 42 (3): 161~165    
    4. 2005 "Preparation of Electrospun Oxidized Cellulose Mats and Their in vitro Degradation Behavior" Macromolecular research 13 (1): 62~67    
    5. 2007 "나노섬유 제조기술" 섬유기술과 산업 = Fiber technology and industry 11 (3): 129~138    
    6. 2010 "규소화 PU/POSS 나노섬유 매트의 물성" 韓國纖維工學會誌 = Textile science and engineering 47 (6): 383~388    
    7. 2010 "용매가 전기방사한 Poly(vinyl acetate)(PVAc) 부직포의 형태 및 기계적 특성에 미치는 영향" 韓國纖維工學會誌 = Textile science and engineering 47 (4): 247~252    
    8. 2010 "경량화 섬유 제조 기술" 섬유기술과 산업 = Fiber technology and industry 14 (1): 1~6    
    9. 2010 "친환경 닥섬유 펄프 자동화 및 닥섬유사 제조 기술" 섬유기술과 산업 = Fiber technology and industry 14 (2): 78~85    
    10. 2011 "열처리 조건이 다른 Poly(lactic acid)(PLA) 직물의 물성 연구" 韓國纖維工學會誌 = Textile science and engineering 48 (2): 116~120    
  • Oh Seung Jin (1)

  • Kim, Hak-Yong (72)

  • 김관우 (3)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기