Macromolecular research v.13 no.2, 2005년, pp.135 - 140   피인용횟수: 2

Aging Effect of Poly(vinyl alcohol) Membranes Crosslinked with Poly(acrylic acid-co-maleic acid)

Rhim Ji Won    (Department of Chemical Engineering, Hannam University   ); Hwang Ho Sang    (Department of Chemical Engineering, Hannam University   ); Kim Dae Sik    (National Research Laboratory for Membranes, School of Chemical Engineering, College of Engineering, Hanyang University   ); Park Ho Bum    (National Research Laboratory for Membranes, School of Chemical Engineering, College of Engineering, Hanyang University   ); Lee Chang Hyun    (National Research Laboratory for Membranes, School of Chemical Engineering, College of Engineering, Hanyang University   ); Lee Young Moo    (National Research Laboratory for Membranes, School of Chemical Engineering, College of Engineering, Hanyang University   ); Moon Go Young    (CRD, Research Park, LG Chem   ); Nam Sang Yong    (Department of Polymer Science and Engineering, Engineering Research Institute, Gyeongsang National University  );
  • 초록

    Poly(vinyl alcohol) (PVA) membranes crosslinked with poly(acrylic acid-co-maleic acid) (PAM) were prepared to investigate the effect of aging on their morphology by swelling them for up to 7 days. PAM was used both as a crosslinking agent and as a donor of the hydrophilic-COOH group. A $30 wt\%$ weight loss of the dry membrane was observed in the swelling test after 6 days. The surface of the membrane was dramatically changed after the swelling test. The surface roughness of the PVA/PAM membrane was increased, as determined by atomic force microscopy (AFM). The swelling loosened the polymer structure, due to the release of the unreacted polymer and the decomposition of the ester bond, thereby resulting in an increase in the free volume capable of containing water molecules. The water molecules present in the form of free water were determined by differential scanning calorimetry (DSC). The fraction of free water increased with increasing swelling time. The swelling of the membrane may provide space for the transport of protons and increase the mobility of the protonic charge carriers. The proton conductivity of the membranes measured at T= 30 and $50^{\circ}C$ was in the range of $10^{-3} to 10^{-2} S/cm$ , and slightly increased with increasing swelling time and temperature.


  • 주제어

    fuel cell .   poly(vinyl alcohol) .   aging effect .   crosslinking .   membrane.  

  • 참고문헌 (16)

    1. J. W. Rhim, C. K. Yeom, and S. W. Kim, J. Appl. Polym. Sci., 68, 1717 (1998) 
    2. T. Yoshida, M. Takahashi, T. Hatakeyama, and H. Hatakeyama, Polymer, 39, 1119 (1998) 
    3. S. Y. Nam, K. S. Sung, S. W. Chon, and J. W. Rhim, Membr. J., 12, 255 (2002) 
    4. A. Higuchi and T. Iijima, Polymer, 26, 1207 (1985) 
    5. H. B. Park, S. Y. Nam, J. W. Rhim, J. M. Lee, S. E. Kim, J. R. Kim, and Y. M. Lee, J. Appl. Polym. Sci., 86, 2611 (2002) 
    6. M. Krumova, D. Lopez, R. Benavente, C. Mijangos, and J. M. Perena, Polymer, 41, 9265 (2000) 
    7. J. W. Rhim and Y. K. Kim, J. Appl. Polym. Sci., 75, 1699 (2000) 
    8. S. J. Kim, C. K. Lee, and S. I. Kim, J. Appl. Polym. Sci., 92, 1467 (2004) 
    9. Y. S. Kim, L. Dong, M. A. Hickner, T. E. Glass, V. Webb, and J. E. McGrath, Macromolecules, 36, 6281 (2003) 
    10. B. S. Pivovar, Y. Wang, and E. L. Cussler, J. Membr. Sci., 154, 155 (1999) 
    11. L. Daniliuc and C. David, Polymer, 37, 5219 (1996) 
    12. J. W. Rhim, S. W. Lee, and Y. K. Kim, J. Appl. Polym. Sci., 85, 1867 (2002) 
    13. J. F. Blanco, Q. T. Nguyen, and P. Schaetzel, J. Membr. Sci., 186, 267 (2001) 
    14. S. Hietala, S. L. Maunu, F. Sundholm, T. Lehtinen, and G. Sundholm, J. Polym. Sci. Part B., 37, 2893 (1999) 
    15. X. Ren, T. E. Springer, and S. Gottesfeld, J. The Electro. Soci., 147, 92 (2000) 
    16. C. Vauclair, P. Schaetzel, R. Nobrega, and C. Habert, J. Appl. Polym. Sci., 86, 1709 (2002) 
  • 이 논문을 인용한 문헌 (2)

    1. Jang, Seo-Won ; Chang, Jin-Hae 2008. "Characterizations of Cellulose Blend Films: Morphology, Mechanical Property, and Gas Permeability" 폴리머 = Polymer (Korea), 32(1): 63~69     
    2. 2008. "" Macromolecular research, 16(6): 555~560     

 저자의 다른 논문

  • 임지원 (88)

    1. 1993 "나일론 4와 이의 블렌드 막을 이용한 에탄올-물 혼합물의 투과 증발분리" 공업화학 = Applied chemistry for engineering 4 (4): 791~797    
    2. 1994 "투과증발 막분리용 모듈의 기술 개발 동향" 멤브레인 = Membrane Journal 4 (4): 187~196    
    3. 1994 "실리콘 막을 이용한 페놀-물 혼합물의 투과 증발 분리" 공업화학 = Applied chemistry for engineering 5 (5): 772~778    
    4. 1995 "역삼투막 공정을 이용한 붕산수 중의 실리카 제거에 관한 연구" 멤브레인 = Membrane Journal 5 (4): 137~144    
    5. 1996 "판틀형 투과증발 막모듈내에서 feed 온도 분포 예측을 위한 모델링" 멤브레인 = Membrane Journal 6 (1): 44~52    
    6. 1999 "복합막 제조를 위한 가교된 폴리비닐알코올 막의 특성 평가와 이를 이용한 투과증발 분리" 멤브레인 = Membrane Journal 9 (3): 157~162    
    7. 1999 "Pervaporation Separation of Trace VOCs from Water Through PDMS Membranes" Korean membrane journal 1 (1): 73~80    
    8. 2000 "Comparison of Pervaporation and Vapor Permeation Separation Processes for MTBE-methanol System" Korean membrane journal 2 (1): 36~47    
    9. 2000 "가교된 PVA 막을 이용한 MTBE/methanol 혼합물의 증기투과(Vapor Permeation)분리" 멤브레인 = Membrane Journal 10 (3): 148~154    
    10. 2001 "투과증발공정을 이용한 물-알코올계에 대한 금속이온이 치환된 이온교환막의 염효과 연구" 멤브레인 = Membrane Journal 11 (3): 133~139    
  • 황호상 (4)

  • 김대식 (1)

  • 박호범 (26)

  • 이창현 (7)

  • Lee, Young-Moo (97)

  • 남상용 (52)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기