Macromolecular research v.13 no.1, 2005년, pp.73 - 79   피인용횟수: 3

Preparation and Characterization of Electrospun Poly(L-lactic acid-co-succinic acid-co-1,4-butane diol) Fibrous Membranes

Jin Hyoung-Joon    (Department of Polymer Science and Engineering, Inha University   ); Hwang Mi-Ok    (Department of Polymer Science and Engineering, Inha University   ); Yoon Jin San    (Department of Polymer Science and Engineering, Inha University   ); Lee Kwang Hee    (Department of Polymer Science and Engineering, Inha University   ); Chin In-Joo    (Department of Polymer Science and Engineering, Inha University   ); Kim Mal-Nam    (Department of Biology, Sangmyung University  );
  • 초록

    Poly(L-lactic acid-co-succinic acid-co-l,4-butane diol) (PLASB) was synthesized by direct condensation copolymerization of L-lactic acid (LA), succinic acid (SA), and 1,4-butanediol (BD) in the bulk using titanium(IV) butoxide as a catalyst. The weight-average molecular weight ofPLASB was $2.1{\times}10^{5}$ when the contents of SA and BD were each 0.5 mol/100 mol of LA. Electrospinning was used to fabricate porous membranes from this newly synthesized bioabsorbable PLASB dissolved in mixed solvents of methylene chloride and dimethylformamide. Scanning electron microscopy (SEM) images indicated that the fiber diameters and nanostructured morphologies of the electrospun membranes depended on the processing parameters, such as the solvent ratioand the polymer concentration. By adjusting both the solvent mixture ratio and the polymer concentration, we could fabricate uniform nanofiber non-woven membranes. Cell proliferation on the electrospun porous PLASB membranes was evaluated using mouse fibroblast cells; we compare these results with those of the cell responses on bulk PLASB films.


  • 주제어

    biodegradable copolymers .   electrospinning .   nanofibers .   non-woven membranes .   scaffolds .   fibroblast cells.  

  • 참고문헌 (61)

    1. S. H. Hyon, F. Z. Jin, K. Jamshidi, S. Tsutsumi, and T. Kanamoto, Macromol. Symp., 197, 355 (2003) 
    2. R. Langer, Acc. Chem. Res., 33, 94 (2000) 
    3. J. V. Seppala, A. O. Helminen, and H. Korhonen, Macromolecular Bioscience, 4, 208 (2004) 
    4. A. L. Yarin, S. Koombhongse, and D. H. Reneker, J. Appl. Phys., 90, 4836 (2001) 
    5. S.-H. Lee, J.-W. Yoon, and M. H. Suh, Macromol. Res., 10, 282 (2002) 
    6. J. A. Matthews, E. D. Boland, G. E. Wnek, D. G. Simpson, and G. L. Bowlin. J. Bioact. Compat. Polym., 18, 125 (2003) 
    7. B. M. Min, G. Lee, S. H. Kim, Y. S. Nam, T. P. Lee, and W. H. Park, Biomaterials, 25, 1289 (2004) 
    8. K. Kim, M. Yu, X. H. Zong, J. Chiu, D. F. Fang, Y. S. Seo, B. S. Hsiao, B. Chu, and M. Hadjiargyrou, Biomaterials, 24, 4977 (2003) 
    9. K. H. Lee, H. Y. Kim, M. S. Khil, Y. M. Ra, and D. R. Lee, Polymer, 44, 1287 (2003) 
    10. L. S. Nair, S. Bhattacharyya, and C. T. Laurencin, Expert Opinion on Biological Therapy, 4, 659 (2004) 
    11. M. Colonna, T. E. Banach, C. Beri, M. Fiorini, E. Marianucci, M. Messori, F. Pilati, and M. Toselli, Polymer, 44, 4773 (2003) 
    12. S. I. Lee, S. C. Yu, and W. S. Lee, Polym. Degrad. Stab., 72, 81 (2001) 
    13. K. M. Huh and Y. H. Bae, Polymer, 40, 6147 (1999) 
    14. Y. Teramoto and Y. Nishio, Polymer, 44, 2701 (2003) 
    15. A. C. Albertsson and I. K. Varma, Biomacromolecules, 4, 1466 (2003) 
    16. I. S. Lee, O. H. Kwon, W. Meng, I.-K. Kang, and Y. Ito, Macromol. Res., 12, 374 (2004) 
    17. Y. M. Shin, M. M. Hohman, M. P. Brenner, and G. C. Rutledge, Polymer, 42, 9955 (2001) 
    18. W. Tan, R. Krishnaraj, and T. A. Desai, Tissue Eng., 7, 203 (2001) 
    19. J. P. Nuutinen, C. Clerc, T. Virta, and P. Tormala, J. Biomat. Sci.-Polym. E, 13, 1325 (2002) 
    20. H.-J. Jin, S. V. Fridrikh, G. C. Rutledge, and D. L. Kaplan, Biomacromolecules, 3, 1233 (2002) 
    21. X. H. Zong, K. Kim, D. Fang, S. Ran, B. S. Hsiao, and B. Chu, Polymer, 43, 4403 (2002) 
    22. W. J. Li, C. T. Laurencin, E. J. Caterson, R. S. Tuan, and F. Ko, J. Biomed. Mater. Res., 60, 613 (2002) 
    23. Z. Zing, X. Y. Xu, X. S. Chen, Q. Z. Liang, X. G. Bian, L. X. Yang, and X. B. Jing, J. Control. Release, 92, 227 (2003) 
    24. H. Fong, I. Chun, and D. H. Reneker, Polymer, 40, 4585 (1999) 
    25. H.-J. Jin, J. Chen, V. Karageorgiou, G. H. Altman, and D. L. Kaplan, Biomaterials, 25, 1039 (2004) 
    26. W. J. Li, K. G. Danielson, P. G. Alexander, and R. S. Tuan, J. Biomed. Mater. Res. Part A, 67A, 1105 (2003) 
    27. H. Winet and J. Bao, J. Biomed. Mater. Res., 40, 567 (1998) 
    28. R. Auras, B. Harte, and S. Selke, Macromolecular Bioscience, 4, 835 (2004) 
    29. L. Calandrelli, G. De Rosa, M. E. Errico, M. I. La Rotonda, P. Laurienzo, M. Malinconico, A. Oliva, and F. Quaglia, J. Biomed. Mater. Res., 62, 244 (2002) 
    30. R. Miyoshi, N. Hashimoto, K. Koyanagi, Y. Sumihiro, and T. Sakai, Int. Polym. Proc., 11, 320 (1996) 
    31. X. H. Zong, S. F. Ran, D. F. Fang, B. S. Hsiao, and B. Chu, Polymer, 44, 4959 (2003) 
    32. E. T. H. Vink, K. R. Rabago, D. A. Glassner, and P. R. Gruber, Polym. Degrad. Stab., 80, 403 (2003) 
    33. L. Huang, R. P. Apkarian, and E. L. Chaikof, Scanning, 23, 372 (2001) 
    34. E. D. Boland, G. E. Wnek, D. G. Simpson, K. J. Pawlowski, and G. L. Bowlin, J. Macromol. Sci.-Pure Appl. Chem., A38, 1231 (2001) 
    35. H. Tsuji and Y. Ikada, Polymer, 36, 2709 (1995) 
    36. L. C. Lu, S. J. Peter, M. D. Lyman, H. L. Lai, S. M. Leite, J. A. Tamada, J. P. Vacanti, R. Langer, and A. G. Mikos, Biomaterials, 21, 1595 (2000) 
    37. Z. M. Huang, Y. Z. Zhang, M. Kotaki, and S. Ramakrishna, Compos. Sci. Technol., 63, 2223 (2003) 
    38. J. D. Stitzel, K. J. Pawlowski, G. L. Bowlin, G. E. Wnek, D. G. Simpson, and G. L. Bowlin, J. Biomater. Appl., 16, 22 (2001) 
    39. K. E. Kadler, D. F. Holmes, J. A. Trotter, and J. A. Chapman, Biochem. J., 316, 71 (1996) 
    40. H. Yoshimoto, Y. M. Shin, H. Terai, and J. P. Vacanti, Biomaterials, 24, 2077 (2003) 
    41. X. Yuan, A. F. T. Mak, and K. Yao, J. Appl. Polym. Sci., 85, 936 (2002) 
    42. S. V. Fridrikh, J. H. Yu, M. P. Brenner, and G. C. Rutledge, Physical Review Letters, 90, 144502 (2003) 
    43. S. Sukigara, M. Gandhi, J. Ayutsede, M. Micklus, and F. Ko, Polymer, 44, 5721 (2003) 
    44. H.-J. Jin, B. Y. Lee, M. N. Kim, and J. S. Yoon, J. Polym. Sci.; Part B: Polym. Phys., 38, 1504 (2000) 
    45. J. A. Matthews, G. E. Wnek, D. G. Simpson, and G. L. Bowlin, Biomacromolecules, 3, 232 (2002) 
    46. Y. K. Luu, K. Kim, B. S. Hsiao, B. Chu, and M. Hadjiargyrou, J. Control. Release, 89, 341 (2003) 
    47. H.-J. Jin, D. S. Kim, B. Y. Lee, M. N. Kim, I. M. Lee, H. S. Lee, and J. S. Yoon, J. Polym. Sci.; Part B: Polym. Phys., 38, 2240 (2000) 
    48. E. E. Boland, J. A. Matthews, K. J. Pawlowski, D. G. Simpson, G. E. Wnek, and G. L. Bowlin, Frontiers in Bioscience, 9, 1422 (2004) 
    49. H.-J. Jin, D. S. Kim, M. L. Kim, I. M. Lee, H. S. Lee, and J. S. Yoon, J. Appl. Polym. Sci., 81, 2219 (2001) 
    50. H.-J. Jin, J. K. Park, K. H. Park, M. N. Kim, and J. S. Yoon, J. Appl. Polym. Sci., 77, 547 (2000) 
    51. P. Makela, T. Pohjonen, P. Tormala, T. Waris, and N. Ashammakhi, Biomaterials, 23, 2587 (2002) 
    52. Y. Ikada and H. Tsuji, Macromol. Rapid Commun., 21, 117 (2000) 
    53. R. Bhardwaj and J. Blanchard, Int. J. Pharm., 170, 109 (1998) 
    54. S. Zarkoob, R. K. Eby, D. H. Reneker, S. D. Hudson, D. Ertley, and W. W. Adams, Polymer, 45, 3973 (2004) 
    55. Y. Wan, W. Chen, J. Yang, J. Bei, and S. Wang, Biomaterials, 24, 2195 (2003) 
    56. S. Sukigara, M. Gandhi, J. Ayutsede, M. Micklus, and F. Ko, Polymer, 45, 3701 (2004) 
    57. W. K. Son, J. H. Youk, and W. H. Park, Biomacromolecules, 5, 197 (2004) 
    58. T. W. Chung, Y. Y. Huang, and Y. Z. Liu, Int. J. Pharm., 212, 161 (2001) 
    59. L. Huang, K. Nagapudi, R. P. Apkarian, and E. L. Chaikof, J. Biomat. Sci.-Polym. E., 12, 979 (2001) 
    60. M. Shin, O. Ishii, T. Sueda, and J. P. Vacanti, Biomaterials, 25, 3717 (2004) 
    61. C. M. Hsu and S. Shivkumar, J. Mater. Sci., 39, 3003 (2004) 
  • 이 논문을 인용한 문헌 (3)

    1. Choi Seung-Eun ; Park Han-Soo ; Lee Kwang-Hee 2006. "Morphology of Membrane of Acrylic Polymers by Wet Phase Inversion Method" 폴리머 = Polymer (Korea), 30(2): 108~111     
    2. 2008. "" Advanced composite materials : the official journal of the Japan Society of Composite Materials and the Korea Society for Composite Materials, 17(2): 157~166     
    3. 2010. "" Macromolecular research, 18(1): 59~66     

 저자의 다른 논문

  • Jin, Hyoung-Joon (14)

    1. 1996 "유화중합이론" 고분자 과학과 기술 = Polymer science and technology 7 (4): 412~424    
    2. 2005 "실크방사" 고분자 과학과 기술 = Polymer science and technology 16 (5): 599~612    
    3. 2006 "단백질계 고분자의 합성 및 응용 - 실크와 엘라스틴 -" 섬유기술과 산업 = Fiber technology and industry 10 (2): 158~173    
    4. 2017 "Li-ion battery anodes from ginkgo leaf-derived nanoporous carbons rich in redox-active heteroatoms" Carbon letters 22 (): 110~114    
  • 윤진산 (8)

  • Lee Kwang Hee (0)

  • Chin, In-Joo (9)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기