방전플라즈마 소결법을 이용한 ZnS-SiO2 복합재료의 제조와 기계적 특성
Fabrication of ZnS-SiO2 Composite and its Mechanical Properties

신대훈   (한양대학교 재료공학부UU0001519  ); 김길수   (한양대학교 재료공학부UU0001519  ); 이영중   (한양대학교 재료공학부UU0001519  ); 조훈   (한국생산기술연구원 나노소재팀CC0186930  ); 김영도   (한양대학교 재료공학부UU0001519  );
  • 초록

    ZnS- $SiO_2$ composite is normally used for sputtering target. In recent years, high sputtering power for higher deposition rate often causes crack formation of the target. Therefore the target material is required that the sintered target material should have high crack resistance, excellent strength and a homogeneous microstructure with high sintered density. In this study, raw ZnS and ZnS- $SiO_2$ powders prepared by a 3-D mixer or high energy ball-milling were successfully densified by spark plasma sintering, the effective densification method of hard-to-sinter materials in a short time. After sintering, the fracture toughness was measured by the indentation fracture (IF) method. Due to the effect of crack deflection by the residual stress occurred by the second phase of fine $SiO_2$ , the hardness and fracture toughness reached to 3.031 GPa and $1.014MPa{\cdot}m^{1/2}$ , respectively.


  • 주제어

    ZnS- $SiO_2$ .   Spark plasma sintering .   High energy ball-milling .   Fracture toughness.  

  • 참고문헌 (16)

    1. M. Horie, T Ohno: Thin Solid Films, 278 (1996) 74-81 
    2. Y. Kageyama, H. Iwasaki, M. Harigaya and Y. Ide: Jpn. J. Appl. Phys., 35 (1996) 500 
    3. M. Terao, A. Hirotsune, Y. Miyauchi, M. Miyamoto, T. Nishida and K. Andoh: Proc. SPIE, 3109 (1997) 60 
    4. G. F. Zhou: Mater. Sci. Eng. A, 304-306 (2001) 73-80 
    5. T. Ueno and Y. Noguchi: U.S. Patent 6,656,260 (2003) 1-8 
    6. W. Luan, L. Gao, H. Kawaoka, T. Sekino and K. Niihara: Ceram. Int., 30 (2004) 405-410 
    7. P. P. Choi, J. S. Kim, O. T. H. Nguyen, D. H. Kwon, Y. S. Kwon and J. C. Kim: Mater. Sci. Eng. A, 449-451 (2007) 1119-1122 
    8. W. H. Rhodes: J. Am. Ceram. Soc., 64 (1981) 19-22 
    9. K. Niihara and R. Morena: Fracture mechanics of solid, Penn. State College, (1981) 
    10. Y. D. Kim, K. Sonezaki, H. Maeda and A. Kato: J. Mat. Sci., 32 (1997) 5101-5106 
    11. G. K. Williamson and W. H. Hall: Acta Metal., 1 (1953) 22 
    12. J. Selsing: J. Am. Ceram. Soc., 44(8) (1961) 419 
    13. S. Donald, Farquhar, Rishi Raj, and S. Leigh Phoenix: J. Am. Ceram. Soc., 73(10) (1990) 3074-80 
    14. Y. Suzuki and K. Niihara: Intermetallics, 6 (1998) 7-13 
    15. H. J. Borg and J. P. Duchateau: Proc. SPIE, 3109 (1997) 20 
    16. M. N. Rahaman and L.C. De Jonghe: J. Am. Ceram. Soc., 70(12) (1987) c348-c351 

 저자의 다른 논문

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 이용한 콘텐츠
이 논문과 함께 출판된 논문 + 더보기