분무열분해공정에 의한 메조기공 알루미나 제조에 있어 Al 전구체 영향
Effect of Al Precursor Type on Mesoporous Alumina Particles Prepared by Spray Pyrolysis

김주현    (공주대학교 화학공학부   ); 정경열    (공주대학교 화학공학부   ); 박균영    (공주대학교 화학공학부  );
  • 초록

    Mesoporous alumina particles were prepared by spray pyrolysis using cetyltrimethyl-ammonium bromide (CTAB) as a structure directing agent and the effect of Al precursor types on the texture properties was studied using $N_2$ adsorption isotherms, small-angle X-ray scattering (SAXS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The surface area and the microstructure of alumina particles were significantly influenced by the Al precursor type. The largest BET surface area was obtained when Al chloride was used, whereas alumina particles prepared from Al acetate had the largest pore volume. According to small-angle X-ray scattering (SAXS) analysis, the alumina powders prepared using nitrate and acetate precursors had a clear single SAXS peak around $2{\theta}=1.0{\sim}1.5^{\circ}$ , indicating that regular mesopores with sponge-like structure were produced. On the basis of TEM, SAXS, and $N_2$ isotherm results, the chloride precursor was most profitable to obtain the largest surface area ( $265\;m^2/g$ ), whereas, the nitrate precursor is useful for the preparation of non-hollow mesoporous alumina with regular pore size, maintaining high surface area ( ${\sim}233\;m^2/g$ ).


  • 주제어

    Mesoporous alumina .   Al precursor .   Spray pyrolysis .   CTAB .   Self assembly.  

  • 참고문헌 (13)

    1. J. Schaep, C. Vandecasteele, B. Peeters, J. Luyten, C.Dotremont and D. Roels: J. Membr. Sci., 163 (1999) 229. 
    2. Y. Kim, C. Kim, I. Choi, S. Rengaraj and J. Yi: Environ. Sci. Technol., 38 (2004) 924. 
    3. R.-H. Zhao, C. P. Li, F. Guo and J.-F. Chen: Ind. Eng. Chem. Res., 46 (2007) 3317. 
    4. M. Kuemmel, D. Grosso, C. Boissiere, B. Smarsly, T.Brezesinski, P. A. Albouy, H. Amenitsch and C.Sanchez: Angew. Chem., Int. Ed., 44 (2005) 4589. 
    5. J. H. Kim, K. Y. Jung, K. Y. Park and S. B. Cho:Micropor. Mesopor. Mater., 128 (2010) 85. 
    6. Y. Lu, H. Fan, A. Stump, T. L. Ward, T. Rieker and C.J. Brinker: Nature, 398 (1999) 223. 
    7. H. Fan, F. V. Swol, Y. Lu and C. J. Brinker: J. Non-Crytal. Solids, 285 (2001) 71. 
    8. G. V. R. Rao, G. P. Lopez, J. Bravo, H. Pham, A. K.Datye, H. Xu and T. L. Ward: Adv. Mater., 14 (2002)1301. 
    9. M. T. Bore, S. B. Rathod, T. L. Ward and A. K. Datye:Langmuir, 19 (2003) 256. 
    10. J. E. Hampsey, S. Arsenault, Q. Hu and Y. Lu: Chem. Mater., 17 (2005) 2475. 
    11. C. Boissiere, L. Nicole, C. Gervais, F. Babonneau, M.Antonietti, H. Amenitsch, C. Sanchez and D. Grosso:Chem. Mater., 18 (2006) 5238. 
    12. Q. Liu, A. Wang, X. Wang and T. Zhang: Micropor. Mesopor. Mater., 100 (2007) 35. 
    13. Q. Liu, A. Wang, X. Wang and T. Zhang: Micropor. Mesopor. Mater., 92 (2006) 10. 

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기