다공성 탄소전극상 무전해 니켈도금의 산성과 알칼리용액 비교 연구
Comparison of Acidic and Alkaline Bath in Electroless Nickel Plating on Porous Carbon Substrate

천소영    (홍익대학교 신소재공학과   ); 강인석    (홍익대학교 신소재공학과   ); 임영목    (한국재료연구소 재료특성평가그룹   ); 김두현    (한국재료연구소 재료특성평가그룹   ); 이재호    (홍익대학교 신소재공학과  );
  • 초록

    Electroless nickel plating on porous carbon substrate for the application of MCFC electrodes was investigated. Acidic and alkaline bath were used for the electroless nickel plating. The pore sizes of carbon substrates were 16-20 ${\mu}m$ and over 20 ${\mu}m$ . The carbon surface was changed from hydrophobic to hydrophilic after immersing the substrate in an ammonia solution for 40 min at $60^{\circ}C$ . The contact angle of water was decreased from $85^{\circ}C$ to less than $20^{\circ}$ after ammonia pretreatment. The deposition rate in the alkaline bath was higher than that in the acidic bath. The deposition rate was increased with increasing pH in both acidic and alkaline bath. The content of phosphorous in nickel deposit was decreased with increasing pH in both acidic and alkaline bath. The contents of phosphorous is low in alkaline bath. The minimum concentration of $PdCl_2$ for the electroless nickel plating was 10 ppm in alkaline bath and 5 ppm in acidic bath. The thickness of nickel was not affected by the concentration of $PdCl_2$ .


  • 주제어

    Electroless nickel plating .   Porous carbon .   Palladium chloride.  

  • 참고문헌 (11)

    1. J. Larminie, A. Dicks, "Fuel Cell Systems Explained", 2nd ed., Willey, 187 (2003) 187. 
    2. K. R. Kull, M. L. Steen, E. R. Fisher, J. Membrance Sci., 246 (2005) 203. 
    3. J. H. Lee, I. G. Lee, T. Kang, N. S. Kim, S. Y. Oh, The Microelectronics and Packaging Society, 10 (2003) 118. 
    4. N. I. Kim, S. S. Jang, "Electroless Plating (無電解鍍金)", 84, DongHwa Technology Publishing Co. All Rights Reserved, (1996) 3. 
    5. J. Hur, "A Study on Electroless Plating of Nickel for Micro-structure Fabrication", Hongik University (1998) 1. 
    6. F. Wang, S. Arai, M. Endo, Carbon, 43 (2005) 1716. 
    7. J. I. Park, J. W. Kim, J. S. Lee, J. of Korean Ind. Eng. Chem., 1 (1990) 224. 
    8. K. K. Kar, D. Sathiyamoorthy, J. of Mater. Processing Technol., 209 (2009) 3022. 
    9. L. Zhou, H. Lin, B. Yi, H. Zhang, Chem. Eng. J., 125 (2007) 187. 
    10. D. Y. Lee, I. S. Lee, S. H. Chang, Electrochimica Acta, 50 (2004) 755. 
    11. X. C. Wang, W. B. Cai, W. J. Wang, H. T. Liu, Z. Z. Yu, Surf. Coat. Technol., 168 (2003) 300. 
  • 이 논문을 인용한 문헌 (1)

    1. Son, Kirak ; Choi, Myung-Hee ; Lee, Kyu Hawn ; Byon, Eungsun ; Rhee, Byong-Ho ; Park, Young-Bae 2016. "Effects of Heat Treatment Conditions on the Interfacial Reactions and Crack Propagation Behaviors in Electroless Ni/electroplated Cr Coatings" 마이크로전자 및 패키징 학회지 = Journal of the Microelectronics and Packaging Society, 23(3): 69~75     

 저자의 다른 논문

  • 천소영 (1)

    1. 2011 "첨가제와 잔류응력이 탄소 기지상 무전해 니켈도금에 미치는 영향" 마이크로전자 및 패키징 학회지 = Journal of the Microelectronics and Packaging Society 18 (4): 43~48    
  • 강인석 (0)

  • 임영목 (13)

  • 김두현 (1)

  • 이재호 (24)

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 이용한 콘텐츠
이 논문과 함께 출판된 논문 + 더보기