Mg과 B 혼합분말을 이용하여 분말압연 공정으로 제조된 $MgB_2$ 초전도 판재연구
$MgB_2$ Sheets using Mixture of Mg and B Powders by Powder Roll Compaction

정국채    (Korea Institute of Materials Science   ); 장세훈    (Korea Institute of Materials Science   ); Sinha, B.B.    (Korea Institute of Materials Science   ); 김정호 ;    (Institute for Superconducting and Electronic Materials, Univ. of Wollongong   );
  • 초록

    $MgB_2$ superconducting sheets have been fabricated by powder rolling method using mixture of Mg and B powders. Sheet-type $MgB_2$ bulk samples of ~10 mm width and 50-100 mm long were squeezed out after compacted by two rotating rolls of 130 mm diameter with gap distance of 0.5 mm and speed of ~40 cm/min (~1 rpm). The nominal composition of Mg, which is ductile metal, was added up to 30% to facilitate forming the $MgB_2$ sheets. The annealed samples at $900^{\circ}C$ and 3 hrs showed superconducting transition temperature of ~32 K and critical current densities at zero fields were ${\sim}10^5A/cm^2$ at 5 K and ${\sim}5{\times}10^4A/cm^2$ at 20 K.


  • 주제어

    $MgB_2$ .   sheet .   powder rolling .   critical current density.  

  • 참고문헌 (5)

    1. V. A. Tracey, Powder Metallurgy 12 (1969) 598. 
    2. D. H. Ro, M. W. Toaz, V. S. Moxson, Journal of Metals (1983) 34. 
    3. K. C. Chung, T. J. Jeong, T. H. Kim, S. T. Ahn, Y. S. Park, D. H. Kim, X. L. Wang, S. X. Dou, Progress in Superconductivity 12(2) (2011) 88.     
    4. Y. Zhang, S. X. Dou, C. Lu, S. H. Zhou, W. X. Li, Physical Review B 81 (2010) 094501. 
    5. J. H. Kim, S. Oh, H. Kumakura, A. Matsumoto, Y. Heo, K. S. Song, Y. M. Kang, M. Maeda, m. Rindfleisch, M. Tomsic, S. Y. Choi, S. X. Dou, Adv. Mater. 23 (2011) 4942. 

 저자의 다른 논문

  • 장세훈 (3)

    1. 2011 "에어로졸 증착법에 의한 $MgB_2$ 박막 제조" Progress in superconductivity 13 (2): 122~126    
    2. 2012 "열처리조건 변화에 따른 in-situ $MgB_2$ 초전도 특성 비교" Progress in superconductivity 14 (2): 116~121    
    3. 2012 "그래핀 나노플레이트에 의한 $MgB_2$의 임계전류밀도 향상" Progress in superconductivity 14 (1): 34~38    

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • NDSL :
유료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기