Transitions in the mechanism of material removal in abrasive wear of alumina

Xu, Hockin H.K. ; Jahanmir, Said ;
  • 초록  

    Abstract The mechanisms of material removal in abrasive wear are investigated by scratching a fine grain alumina with a diamond indenter. Subsurface damage is examined as a function of load and number of passes using a bonded-interface sectioning technique together with microscopy. Scratching produces classical lateral and median cracks extending from the plastic zone beneath the contact area. Damage within the plastic zone is distributed in nature taking the form of intragrain twin/slip bands and intergranular microcracks. Repeated scratching causes damage accumulation in the material beneath the sliding contact area. After a critical number of passes, a transition is observed from a damage accumulation process to a material removal process that involves mainly grain dislodgement. As the number of passes is increased at large loads, the removal process exhibits a second transition from grain dislodgement to a more severe wear process by lateral crack chipping.


  • 주제어

    Abrasive wear .   Alumina .   Grain dislodgement .   Lateral crack chipping .   Material removal .   Scratching .   Wear transition.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기