Adhesion at the polypropylene/liquid crystalline polymer blend-glass interface

Lipatov, Yuri S. ; Shumsky, Vadim F. ; Babich, Valentin F. ;
  • 초록  

    Abstract The adhesion of a blend of liquid-crystalline polymer (LCP) with polypropylene (PP) to the surface of glass fibres has been investigated in the whole range of blend composition. It was found that the composition dependence of the adhesion strength is characterized by a sharp increase when the amount of LCP in the blend exceeds a definite limit corresponding to phase inversion. The results are explained by the formation near the interface of two adhesion layers: the first is composed of pure LCP and has a higher surface tension, whereas the second layer represents the blend of varying composition. At small amounts of LCP adhesion failure proceeds in the interphase between the LCP and the blend. After phase inversion, where the adhesion strongly increases, adhesion failure proceeds near the interface between the LCP and the glass.


  • 원문보기

    원문보기
    무료다운로드 유료다운로드
    • 원문이 없습니다.

    유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

  • 주제어

    polymer blends .   glass substrate .   adhesion phase inversion .   interphase .   filled blend.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역