Step density dependence of co2 reduction rate on Pt(S)-[n(111) × (111)] single crystal electrodes

Hoshi, Nagahiro ; Suzuki, Toshitake ; Hori, Yoshio ;
  • 초록  

    Abstract CO 2 reduction was studied by voltammetry with Pt single crystal electrodes of Pt(S)-[ n (111) × (111)] at constant potentials. The rate of CO formation depends on crystal orientation as below; Pt(110) > Pt(331) > Pt(221) > Pt(332) > Pt(997) > Pt(111). The initial rates of the CO formation plotted against the amount of adsorbed hydrogen ( Q H 0 ) gave a maximum of around Q H 0 = 40 μCcm − 2 on the electrodes with high step density, Pt(110), Pt(331) and Pt(221), whereas the electrodes with low step density, Pt(332), Pt(997) and Pt(111), showed monotonous increase with Q H 0 . The activity series shown above was well correlated with the step density of crystal orientations except Pt(110)(1 × 2). The correlation and the anomalously high activity of Pt(110) are discussed with regard to the adsorption sites for hydrogen atoms with reference to UHV works in literatures. Reduction of CO 2 proceeds with adsorbed hydrogen regenerated on the adsorption sites.


  • 원문보기

    원문보기
    무료다운로드 유료다운로드
    • 원문이 없습니다.

    유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

  • 주제어

    reduction of CO2 .   CO formation rate .   Pt single crystal .   step density .   Pt(S)-[n(111) × (111)].  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역