Moisture effects on Mode II delamination behavior of carbon/epoxy composites

Zhao, Sh.    (Beijing Univ of Aeronautics and AstronauticsChina  ); Gaedke, M.  
  • 초록

    Moisture effects on Mode II interlaminar fracture in T300/914C and T300/M10 carbon/epoxy composites were investigated by using ENF specimens exposed to different hydrothermal conditions. Crack growth behavior, interlaminar shear strength, glass transition temperature and fractographs of the materials were examined toward establishing the possible mechanisms of moisture effects. It was found that Mode II fracture toughness of T300/M10 is more sensitive to moisture than that of T300/914C. For T300/914C, the matrix was plasticized by water and thus G IIc > increased slightly. With further moisture absorption, swelling action weakened the interface and led to reduction of fracture toughness. For T300 M10, moisture primarily weakened the interfacial strength and resulted in decrease in G IIc >. It seemed that water plasticization contributed to the enhancement of delamination toughness of the fiber-matrix system with strong interface, and degraded the toughness of the system with weak interface due to a decrease of the fracture area. However, for both of the two systems, the swelling action, which weakened the interface bond, always reduced the delamination resistance.(Author abstract)


 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기