Biomimetic apatite induction on Ca-containing titania

  • 초록

    To understand the apatite induction mechanism in SBF, Ca-containing titania film without CaTiO 3 phase was fabricated by micro-arc oxidation (MAO) at low voltage (230V) in an electrolytic solution containing calcium acetate monohydrate. Macro-porous, Ca-containing titania film was formed on the titanium substrate and the oxidized layer was composed of anatase and rutile phase. When immersed in 1.5SBF, no apatite was induced in the MAO specimen similar to the CaTiO 3 -containing titania. However, after hydrothermal treatment at 250 o C for 2h, numerous precipitates, presumably calcium phosphates, were formed on the surface of the titania after 7day immersion and titania surface was entirely covered with apatite after 14 days of immersion. This study clearly showed that Ca-containing titania has the capability to induce apatite in SBF and hydrothermal treatment plays a decisive role in apatite induction, particularly producing surface hydroxyl groups such as Ca-OH or Ti-OH.


 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기