Preparation of β-Ca3(PO4)2 bioceramic powder from calcium carbonate and phosphoric acid

  • 초록

    When preparing β-tricalcium phosphate (β-TCP) with Ca(NO 3 ) 2 or Ca(OH) 2 as the raw materials, because of the problem of filtering, it is difficult to industrialize traditional methods. In this paper, β-TCP was prepared with calcium carbonate and phosphoric acid. According to XRD spectrum, the precursor of this system is octacalcium phosphate (OCP) [Ca 8 H 2 (PO 4 ) 6 .5H 2 O] instead of non-stoichiometric hydroxyapatite (HA) obtained from traditional methods, and thermodynamics mechanism of the reaction was also studied. The crystal β-TCP powders were obtained after the precursor had been calcined at 850-1150 o C for 2h. SEM images showed that hardening could eliminate the reunion to a great extent, and obtain dispersive β-TCP powders with a particle diameter between 0.5 and 2.0μm. The main advantages of this process over traditional methods are the fast reaction rate, the easy filtering, the fine particle size and the minimum impurity.


 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기