Influence of K2TiF6 in electrolyte on characteristics of the microarc oxidation coating on aluminum alloy

Tang, M.    (Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, 37# Xueyuan Road, Haidian District, Beijing 100191, China  ); Li, W.   Liu, H.   Zhu, L.  
  • 초록

    Black and gray microarc oxidation (MAO) coatings were prepared in a phosphate electrolyte with and without K 2 TiF 6 on 2A70 aluminum alloy, respectively. Voltage-time curves were recorded during the MAO process. The effects of K 2 TiF 6 on the morphology, composition, abrasive resistance and corrosion resistance of MAO coatings were investigated. The results showed that the MAO coating produced in the electrolyte with K 2 TiF 6 was thicker, and more uniform than that produced in the electrolyte without K 2 TiF 6 . Ti was detected in the surface of the MAO coating formed in the electrolyte with K 2 TiF 6 . The results of abrasive resistance and corrosion resistance showed that the MAO coating formed in the electrolyte with K 2 TiF 6 exhibited better abrasive resistance and corrosion resistance.


  • 주제어

    Aluminum alloy .   Microarc oxidation .   Black MAO coating .   Abrasive resistance .   Corrosion resistance.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기