Composite structures v.163, 2017년, pp.123 - 128  

Fracture behavior and strain evolution of laminated composites

Wu, H. ; Fan, G. ; Huang, M. ; Geng, L. ; Cui, X. ; Chen, R. ; Peng, G. ;
  • 초록  

    Laminated composites consisting of alternating layers of TiB w /Ti and Ti(Al) were prepared, and exhibited a superior elongation to fracture that is nearly 20 times higher than that of bulk TiB w /Ti composites. Coupling two- and three-dimensional fracture characterizations of TiB w /Ti-Ti(Al) laminated composites show distinct fracture characteristics including crack distribution, formation of tunnel cracks, and suppression of crack propagation. These experimentally observed fracture characteristics are intimately correlated with in situ monitored strain evolution process, by which we observed that strain localization is effectively suppressed by laminated structure, thus lowering the stress intensity near the crack tip as well as the driving force for crack propagation. As a consequence, laminated composites are not so sensitive to the early cracking, and exhibit a good strength-ductility combination.


  • 주제어

    Laminated structures .   Image analysis .   Fracture .   Strain delocalization .   Digital image correlation (DIC).  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기