Composite structures v.163, 2017년, pp.257 - 266  

Influence of drilling and abrasive water jet induced damage on the performance of carbon fabric/epoxy plates with holes

Montesano, J. ; Bougherara, H. ; Fawaz, Z. ;
  • 초록  

    The influence of conventional drilling (CD) and abrasive water jet (AWJ) cutting on the fatigue performance of carbon fabric/epoxy plates was investigated. Observations of machined hole regions revealed more severe damage on the CD hole surfaces with larger damage regions penetrating into the material. For both material systems investigated, the surface roughness for AWJ holes was in fact higher in comparison to CD holes. Nonetheless, static properties, short-term fatigue properties and endurance limits of the plates were not affected by the machining technique. Observed damage, stiffness and temperature evolutions during short-duration cyclic tests showed no significant changes in fatigue response for CD and AWJ plates, suggesting that surface roughness is not a good indicator of hole quality. However, long-duration cyclic tests revealed that CD plates exhibited greater stiffness degradation and advanced damage after a cyclic threshold, beyond which machining-induced delamination cracks began to propagate. This was not observed for the AWJ plates, where instead cyclic loading-induced delamination cracks initiated and propagated much later. These key findings are critical for assessing the unique performance characteristics of fabric/epoxy plates with holes. Since these materials are increasingly used for primary fatigue-critical structures, the presented outcomes are vital for designing corresponding structure joining methods.


  • 주제어

    Fabric carbon fiber/epoxy .   Fatigue .   Thermography .   Water jet .   Drilling .   Damage.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기