Preparation and characterization of glass foams for artificial floating island from waste glass and Li2CO3
Abstract In this work, a type of glass foam for artificial floating island applications was produced from solid waste glass by using powder sintering technology at a low temperature using Li 2 CO 3 as the foaming agent. The effects of Li 2 CO 3 content and foaming temperature on the microstructure, crystalline phase composition and macroscopic properties of glass foams were investigated. The results showed that the optimal glass foam with homogeneous porous structure, low bulk density (0.32g/cm 3 ), and high compressive strength (2.64MPa) could be prepared under conditions of 7wt% Li 2 CO 3 content and sintering at 750°C. In addition, the water and acid resistance experiments for the obtained optimized samples indicated that the final product possessed excellent chemical stability. Highlights Waste glass and Li 2 CO 3 were used as raw material and foaming agent respectively. Li 2 CO 3 content and foaming temperatures affected the structures and properties. Prepared glass foams possessed good chemical stability for the application. Graphical abstract This figure shows the influence of Li 2 CO 3 content and foaming temperature on the microstructure and properties of glass foams (Llaudis et al., 2009). The arrangement of pictures in Graphical Abstract is inspired by Llaudis et al. In that paper, the SEM images shown in illustrate the microstructure of glass foams with different temperature and soaking time, which give us great inspiration. In order to summarize and highlight the results of our work, we arranged the SEM images in that way and combined the figure of properties to show the influence of Li 2 CO 3 content and foaming temperatures on the microstructures, bulk densities and compressive strength. [DISPLAY OMISSION]
- 원문이 없습니다.
- DOI : http://dx.doi.org/10.1016/j.conbuildmat.2016.12.048
- Elsevier : 저널> 권호 > 논문
유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.
원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.
NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.
- 이 논문과 함께 출판된 논문 + 더보기