Fracture toughness and hydrogen embrittlement susceptibility on the interface of clad steel pipes with and without a Ni-interlayer

Jemblie, L. (Department of Engineering Design and Materials, NTNU, 7456 Trondheim, Norway ); Bjaaland, H. (Department of Engineering Design and Materials, NTNU, 7456 Trondheim, Norway ); Nyhus, B. (SINTEF Materials and Chemistry, 7456 Trondheim, Norway ); Olden, V. (SINTEF Materials and Chemistry, 7456 Trondheim, Norway ); Akselsen, O.M. (Department of Engineering Design and Materials, NTNU, 7456 Trondheim, Norway );
  • 초록  

    Abstract The objective of the present work has been to study the fracture properties of the interface between clad and base material of two 316L austenitic stainless steel - X60/X65 carbon steel hot roll bonded clad pipes; with and without a Ni-interlayer. Fracture mechanical tests were performed in air and under in situ electrochemical hydrogen charging to establish crack growth resistance curves and fracture initiation toughness for both systems. The results revealed that an electroplated Ni-interlayer reduces the fracture initiation toughness for testing in air, while it raises the fracture initiation toughness for testing in hydrogen environment. The samples with a Ni-interlayer revealed little influence of hydrogen on the fracture resistance, with a reduction in the fracture initiation toughness of 20%, attributed to crack propagation mainly occurring in the nickel layer. The samples without a Ni-interlayer revealed a strong influence of hydrogen on the fracture resistance, with a reduction in the fracture initiation toughness of 85%. An alternating crack path was proven, shifting between the dissimilar interface and the base material adjacent to the interface.


  • 주제어

    Clad pipe .   Cladding .   Hydrogen embrittlement .   Fracture toughness .   Electroplating .   Interface.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기