Ceramics international v.43 no.6, 2017년, pp.4746 - 4752   SCI SCIE SCOPUS
본 등재정보는 저널의 등재정보를 참고하여 보여주는 베타서비스로 정확한 논문의 등재여부는 등재기관에 확인하시기 바랍니다.

Magnetic properties and hyperfine interactions of Co1-2xNixMnxFe2O4 nanoparticles

Baykal, A. (EYRA Textile Chemicals and Chemical Industry Trade Company, Saraçlar Industrial Zone, No:3-12, 34490, İkitelli-İstanbul/TURKEY ) ; Eryiğit, Ş. (Department of Chemistry, Middle East Technical University, 06500 Çankaya, Ankara, Turkey ) ; Topkaya, R. (Department of Electrical Electronic Engineering, Iğdır University, 76000 Iğdır, Turkey ) ; Güngüneş, H. (Department of Physics, Hitit University, 19030 Çevre Yolu Bulvarı, Çorum, Turkey ) ; Amir, Md. (Department of Chemistry, İstanbul University, Avcılar, İstanbul, Turkey ) ; Yıldız, A. (Department of Textile Engineering, Namık Kemal University, 59860 Çorlu, Tekirdag, Turkey ) ; Kurtan, U. (Department of Chemistry, İstanbul University, Avcılar, İstanbul, Turkey ) ; Shirsath, Sagar E. (Spin Device Technology Center, Faculty of Engineering, Shinshu University, 380-8553 Nagano, Japan ) ;
  • 초록  

    Abstract Co1-2xNixMnxFe2O4 (0.0≤x≤0.5) nanoparticles (NPs) were prepared via citrate assisted microwave combustion route. XRD analysis confirmed the cubic structure (spinel) of all samples. Average crystallite size of products (obtained from (311) diffraction line) was in the range of 32.9–43.4nm. The intense peak appearing at around 531cm −1 in FT-IR was attributed to the formation of a spinel ferrite. Magnetic properties of the products were investigated by room temperature vibrating sample magnetometer and MOssbauer spectroscopy. The magnetic parameters have been found to strongly depend on the Ni and Mn concentrations. The saturation magnetization continuously decreases with the increasing of the concentration (x). We found that Ni 0.5 Mn 0.5 Fe 2 O 4 NP has superparamagnetic character at room temperature. This result was also verified by MOssbauer analysis. Scanning electron microscopic analysis revealed the cubic morphology of all products, EDX and elemental mapping analyses confirmed the expected composition of each product.


  • 주제어

    Magnetic nanomaterials .   Superparamagnetism .   Spinel .   Hyperfine interactions.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기