Influence of injection temperature and pressure on the properties of alumina parts fabricated by low pressure injection molding (LPIM)

Sardarian, M. (Corresponding author. ); Mirzaee, O. ( ); Habibolahzadeh, A. ( );
  • 초록  

    Abstract The quality of ceramics parts made by powder injection molding (PIM) method is influenced by a range of factors such as powder and binder characteristics, rheological behavior of feedstock, molding parameters and debinding and sintering conditions. In this study, to optimize the molding parameters, the effect of injection temperature and pressure on the properties of alumina ceramics in the LPIM process were thoroughly studied. Experimental tests were conducted on alumina feedstock with 60vol% powder. Injection molding was carried out at temperatures and pressures of 70–100°C and 0.1–0.6MPa respectively. Results showed that increase in injection temperature and pressure and the resulting increase in flow rate leads to the formation of void which impairs the properties of molded parts. The SEM studies showed that injection at temperature of 100°C results in evaporation of binder components. From the processing point of view, the temperature of 80°C and pressure of 0.6MPa seems to be the most suitable condition for injection molding. In addition, the effects of sintering conditions (temperature and time) on the microstructure and mechanical properties are discussed. The best final properties were found using injection molding under the above stated conditions, thermal debinding and sintering at 1700°C during 3h.


  • 주제어

    Alumina .   Low pressure injection molding .   Sintering .   Defect .   Flexural strength.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기