Effect of UV irradiation on magnetic behavior of reduced graphene oxide decorated with nickel nanostructure

Sharma, Geeta (Mechanical Metallurgy Division, Bhabha Atomic Research Centre, Mumbai, India ) ; Gosavi, S.W. (Dept. of Physics, Savitribai Phule Pune University, Pune, India ) ;
  • 초록  

    Abstract Reduced graphene oxide (RGO) decorated with nickel has been synthesized via an in-situ reduction of graphene oxide (GO) and nickel nitrate using NaOH and hydrazine. The starting materials Ni (NO 3 ) 2 and GO were taken in two different ratios and the products formed were designated as RGNi 2 and RGNi 1 . The formation of the composite was confirmed by the appearance of X-ray diffraction peaks at 44.5°, 51.9°, 76.5° corresponding to Ni and at 24.8°and 43.2° for RGO. The RGNi 2 was irradiated with UV light (λ=254nm) for different durations (2, 6, 12, 24 and 48h). Intensity ratio of d and g-bands (I d /I g ) of Raman spectra increases from 1.18 to 1.47 over the duration of irradiation period (2–48h). The magnetization measurements using the vibrating sample magnetometer (VSM) of these samples reveal their ferromagnetic behavior. The calculated saturation magnetization (M S ) value of Ni, RGNi 1 and RGNi 2 is 47.86, 30.56 and 8.25emu/g respectively and the corresponding coercivity (H C ) value is found to be 181, 227 and 296Oe. The M S of RGNi 2 is found to increase to 10.65emu/g after 48h of irradiation. This enhancement in the M S (~23%) with irradiation may be due to defect formation by the UV light.


  • 주제어

    Graphene .   Composite .   Magnetism .   UV-irradiation.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기