Fabrication of Mn3O4–carbon nanotube composites with high areal capacitance using cationic and anionic dispersants

Ata, M.S.    (Corresponding author.  ); Milne, J.   Zhitomirsky, I.  
  • 초록  

    Abstract Mn 3 O 4 -multiwalled carbon nanotube (MWCNT) electrodes for supercapacitors with high active mass loadings have been fabricated with the goal of achieving a high area normalized capacitance (C S ) and enhanced capacitance retention at high charge-discharge rates. Poly(4-styrenesulfonic acid- co -maleic acid) sodium salt P(SSA-MA) was used as a charging and dispersing agent for the fabrication of Mn 3 O 4 . The unique bonding properties of the MA monomers allowed efficient P(SSA-MA) adsorption on Mn 3 O 4 , whereas SSA monomers imparted a negative charge. Cationic ethyl violet (EV) and pyronin Y (PY) dyes were used for dispersion and charging of MWCNT. Good dispersion of the individual components and their electrostatic heterocoagulation facilitated efficient mixing, which allowed enhanced capacitive behavior at mass loadings of 28.4 mg cm −2 , which meet requirements for practical applications. The highest capacitance of 2.8 F cm −2 was obtained at a scan rate of 2 mV s −1 for the composites, prepared using PY. However, the composites, prepared using EV showed better capacitance retention of 88% in the scan rate range of 2–100 mV s −1 and the capacitance of 2.1 F cm −2 was obtained at a scan rate of 100 mV s −1 . The composites showed activation behavior during cycling, which resulted in a capacitance increase and electrical resistance reduction. The results of this investigation showed that Mn 3 O 4 –MWCNT composites, prepared by new colloidal methods are promising materials for practical applications in electrochemical supercapacitors. Graphical abstract [DISPLAY OMISSION]


  • 주제어

    Manganese oxide .   Supercapacitor .   Carbon nanotube .   Composite .   Capacitance .   Impedance.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
  • 원문이 없습니다.
유료다운로드

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기