Surface Evolution of Nano-Textured 4H–SiC Homoepitaxial Layers after High Temperature Treatments: Morphology Characterization and Graphene Growth

Liu, Xingfang    (Key Laboratory of Semiconductor Materials Science, Institute of Semiconductors, Chinese Academy of Sciences, P.O. Box 912, Beijing 100083, China  ); Chen, Yu    (E-Mails: guanmin@semi.ac.cn (M.G.)  ); Sun, Changzheng    (zhang_yang@semi.ac.cn (Y.Z.)  ); Guan, Min    (fzhang@semi.ac.cn (F.Z.)  ); Zhang, Yang    (gshsun@semi.ac.cn (G.S.)  ); Zhang, Feng    (ypzeng@semi.ac.cn (Y.Z.)   ); Sun, Guosheng    (Semiconductor Lighting Technology Research and Development Center, Institute of Semiconductors, Chinese Academy of Sciences, P.O. Box 912, Beijing 100083, China   ); Zeng, Yiping    (Tsinghua National Laboratory for Information Science and Technology, Tsinghua University, Beijing 100084, China  );
  • 초록  

    Nano-textured 4H–SiC homoepitaxial layers (NSiCLs) were grown on 4H–SiC(0001) substrates using a low pressure chemical vapor deposition technique (LPCVD), and subsequently were subjected to high temperature treatments (HTTs) for investigation of their surface morphology evolution and graphene growth. It was found that continuously distributed nano-scale patterns formed on NSiCLs which were about submicrons in-plane and about 100 nanometers out-of-plane in size. After HTTs under vacuum, pattern sizes reduced, and the sizes of the remains were inversely proportional to the treatment time. Referring to Raman spectra, the establishment of multi-layer graphene (MLG) on NSiCL surfaces was observed. MLG with sp 2 disorders was obtained from NSiCLs after a high temperature treatment under vacuum at 1700 K for two hours, while MLG without sp 2 disorders was obtained under Ar atmosphere at 1900 K.


  • 주제어

    nano-textured .   4H–SiC .   morphology .   graphene .   evolution.  

 활용도 분석

  • 상세보기

    amChart 영역
  • 원문보기

    amChart 영역

원문보기

무료다운로드
유료다운로드
  • 원문이 없습니다.

유료 다운로드의 경우 해당 사이트의 정책에 따라 신규 회원가입, 로그인, 유료 구매 등이 필요할 수 있습니다. 해당 사이트에서 발생하는 귀하의 모든 정보활동은 NDSL의 서비스 정책과 무관합니다.

원문복사신청을 하시면, 일부 해외 인쇄학술지의 경우 외국학술지지원센터(FRIC)에서
무료 원문복사 서비스를 제공합니다.

NDSL에서는 해당 원문을 복사서비스하고 있습니다. 위의 원문복사신청 또는 장바구니 담기를 통하여 원문복사서비스 이용이 가능합니다.

이 논문과 함께 출판된 논문 + 더보기