요업학회지 = Journal of the Korean Ceramic Society 11건

  1. [국내논문]   탄소피막 저항기용 자기소체 제조에 있어 Barite 활용에 관한 연구  

    박정현 (연세대학교 요업공학과 ) , 전병세 (연세대학교 요업공학과 ) , 배원태 (연세대학교 요업공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 95 - 100 , 1982 , 1225-1372 ,

    초록

    Instead of barium carbonate, domestic barite was used as the flux in manufacturing theinsulating porcelain. To avoid the problems arising from the decomposition of barite in the body during firing, BaO. $Al_2O_3$ was synthesized at $1300^{\circ}C$ for 5 hours. synthetic BaO. $Al_2O_3$ was mixed with other materials such as kaoline, alumina, clay, dolomite. The RO content (CaO. MgO. BaO) of the batches was varied from range of 4 to 14wt. % at 2wt. % - intervals, and firing temperature was varied from 1280 to 140 $0^{\circ}C$ -at 4 $0^{\circ}C$ intervals The properties such as water absorption, bulk density. mechnical strength, specific resistance, and linear shrinkage were measured. The body containing 12 wt.% of RO content showed the satisfactory for the application in the Fixed Carbon Film Resistor.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  2. [국내논문]   천연 규회석을 이용한 신속소성소지 구성에 관한 연구  

    안영필 (한양대학교 무기재료 공학과 ) , 최의석 (한양대학교 무기재료 공학과 ) , 김복희 (한양대학교 무기재료 공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 101 - 108 , 1982 , 1225-1372 ,

    초록

    As raw materials wollastonite, kaolin and pyrophyllite were used to synthesize mullite, anorthite and pseudowoll-astonite which were known as low thermal expansion substance. Increasing the amount of wollastonite in the composition resulted in a linear thermal expansion behavior. However, the increases of pyrophyllite indicated the relatively unstable themmal expansion behavior, because the phase transition occured in quartz of the pyrophyllite compositon. To lowering sintering temperature feldspar (Kebook and Anyang) were added in the composition that showed the linear thermal expantion behavior, and over 50'C were lowered.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  3. [국내논문]   불소운모의 결정화   피인용횟수: 1

    송경근 (한양대학교 무기재료공학과 ) , 오근호 (한양대학교 무기재료공학과 ) , 이경희 (명지대학 요업공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 109 - 114 , 1982 , 1225-1372 ,

    초록

    Fluoro-phlogopite crystals (Mica) were synthesized by two different methods; firstly the crystal was crystallized from the melts, and secondly mica crystalline was obtained from the direct solid state reaction. Addition of $CaF_2$ in the mica batch revealed the lowering the solid state reaction temperature. SEM and XRD were employed to observe mica crystalline flakes and solid solution forms. As a starting raw material Pyrophyllite was used resulting in the formation of mica crystals.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  4. [국내논문]   $Si_3N_4$ 결합 SiC 내화재료에 있어서 생성된 $Si_3N_4$의 미구조 변화   피인용횟수: 1

    최덕균 (한국과학기술원 요업재료연구실 ) , 이준근 (한국과학기술원 요업재료연구실)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 121 - 126 , 1982 , 1225-1372 ,

    초록

    This paper deals with the $Si_3N_4$ -bonded SiC refractory in terms of its microstructure development during nitridation. When mixture of SiC grains and fine Si power is fired under nitrogen atmosphere, an interlocking network of $Si_3N_4$ whiskers is formed by nitridation of Si. It is found that the strength of $Si_3N_4$ -bonded SiC refractory is soley due to the physical nature of this interlocking whiskers. At the initial stage of nitridation, $Si_3N_4$ whisker forms in very thin and long shape and, with further nitridation, it becomes thicker with diameters up to 0.35 $\mu\textrm{m}$ . It is found that the mechanical strength of $Si_3N_4$ -bonded SiC refractory depends on the degree of nitridation and the development of microstructure.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  5. [국내논문]   마그네시아의 치밀화 및 입자성장에 미치는 첨가물의 영향  

    이해원 (서울대학교 요업공학과 ) , 김환 (서울대학교 요업공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 127 - 132 , 1982 , 1225-1372 ,

    초록

    This experiment has been carried out for the purpose of investigating the effect of additives on densification and grain growth in magnesium oxide by a two-step process; hot pressing and heat treating. MgO powder has been obtained by calcining extra reagent grade MgCO3 at 90 $0^{\circ}C$ for 30 minutes, and additives have been added to $MgCO_3$ in the form of soluble salts-Al $(NO_3)_3$$ . $9H_2O$ and $Cr(NO_3)_3$ . 9H_2O$ . The hot pressing has been carried out with changes of soaking time at 125 $0^{\circ}C$ under the pressure of 250kg/ $\textrm{cm}^2$ , and the heat treating also at same temperature. The initial particle size of MgO measured by particle size analyzer was 0.86 microns. Densification rate obeyed the equation D=K lnt + C, and grain growth rate obeyed the equation G-G0=kt1/2. It was vaporization of some $Cr_2O_3$ and formation of solid solution that had an influence on desification of MgO containing $Cr_2O_3$ . Activation energy for grain growth of pure MgO was 62.4 kcal/mole, therefore grain growth was supposed to be diffusioncontrolled process. But after heat treatmeat, excess additives were expected to slow down the grain growth by the formation of second phase or the solute atoms at grainboundary.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  6. [국내논문]   Tricalciumaluminate의 초기 수화반응에 미치는 $K_2O$의 영향  

    한기성 (인하대학교 공과대학 무기재료공학과 ) , 최만 (쌍용양회중앙연구소 ) , 서일영 (쌍용양회중앙연구소)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 133 - 138 , 1982 , 1225-1372 ,

    초록

    Two kinds of clinker liquid melts, one containing 2.0% of $K_2O$ and the other without $K_2O$ , were prepared with the similar composition as those developed during the firing of portland cement clinker. One portion of melt was quenched and found to consist of glass together with traces of proto- $C_3A$ , and the other portion was allowed to cool spontaneously to crystallize $C_3A$ and calciumferrite well. The product obtained by crystallization of the melt without $K_2O$ showed cubic $C_3A$ , while orthorhombic $C_3A$ was formed from the crystallized product containing $K_2O$ . Studies on the hydration behavior of the samples made from the melts with 30% of gypsum were carried out for 24 hours by observation at regular intervals ettringite, monosulphate hydrates and gypsum which were formed or consumed during hydration. The samples without $K_2O$ in the melts were hydrated wth addition of proper amount of $K_2SO_4$ in the water for hydration. Hydration behavior of glassified $C_3A$ showed that it has low reactivity relative to crystallized $C_3A$ , and also hydration reactivity of orthorhombic $C_3A$ was much lower than that of cubic $C_3A$ in 60 minutes. Potassium sulphate in the solution reduced the hydration reactivity of $C_3A$ . Evolution peaks of hydration heat examined by twin-type conduction micro-calorimeter showed that glassified $C_3A$ without $K_2O$ had secondary peak after 9 hours and $C_3A$ containing $K_2O$ after 12 hours. When crystallized $C_3A$ was hydrated, initial peaks of hydration heat were considerably high and there was no secondary peak for cubic $C_3A$ but the secondary peak of orthorhombic $C_3A$ appeared after 4 hours.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  7. [국내논문]   $MgO-SiO_2$계 자기에 관한 연구   피인용횟수: 2

    이응상 (한양대학교 무기재료공학과 ) , 이종근 (한양대학교 무기재료공학과 ) , 임대영 (한양대학교 무기재료공학과 ) , 최성철 (한양대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 139 - 144 , 1982 , 1225-1372 ,

    초록

    This study has examined closely on the various foundamental conditions for the fitting in steatite porcelain as a industrial porcelain of superior quality, and as a decorated porcelain. The materials consisting of the Kyul Sung talc, and the sea water magnesia clinker power which was produced from Sam Hwa-Hwa Sung, as major constituents have been used, and also used Hyup Jin kaolin as clay minerals to give them plasticity. First, the mixture was made of corresponding in the theoretical composition of enstatite with Kyul sung talc and sea water magnesia clinker, and kaolin was added in various kinds of 1%, 2.5% 5%, 10%, and 20% by weight of the mixture. Next, the mixture was fired at the various temperatures from 1330 to 145 $0^{\circ}C$ . After we examined closely the physical properties and microstructures, we achieved the results that noted from this study were listed below. 1. The addition amount of kaolin should generally be from 5% to 10% by weight of the mixture to give mixture plasticity in steatite porcelain, but preferably about 20% to consider the firing temperature. 2. The temperature of the optimum firing range is from 1390 C to 142 $0^{\circ}C$ . 3. A case, which the $A_2$ composition had been fired at 142 $0^{\circ}C$ , showed a good effect in the strength, but showed a bad result in the absorption. Therefore, the specimens of $A_4$ the composition has excellent in properties of matters when the composition is fired at 142 $0^{\circ}C$ . Also, we consider that the specimens of the $A_5$ composition, which is fired at 139 $0^{\circ}C$ , is suitable for the $MgO-SiO_2$ porcelain bodies with respect to the various properties.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  8. [국내논문]   알카리토금속 화합물에 의한 루테늄의 흡착  

    류경옥 (한양대학교 공과대학 화학공학과 ) , 문세기 (한양대학교 공과대학 화학공학과 ) , 이근범 (한양대학교 공과대학 화학공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 145 - 151 , 1982 , 1225-1372 ,

    초록

    Many materials such as silica gel, metallic oxide, activated alumina and alkaline earth metal carbonates were employed as filter media for gaseous oxides of ruthenium volatilized during high level radioactive waste processing. The adsorption efficiency of ruthenium on these materials was evaluated. For the purpose of observing behavior of ruthenium oxides, thermogravimetric analysis of ruthenium oxide in a stream of oxygen was carried out. The rate of volatilization was proportional to the square root of oxygen partial pressure, and increased exponentially with temperature. At $650^{\circ}C$ , gaseous ruthenium oxides showed a strongly marked effect of deposition. Of all the materials available, calcium oxide proved to be the best that could be used to adsorb ruthenium.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  9. [국내논문]   Hot Press에 의한 마그네시아의 소결  

    오기동 (부산대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 152 - 156 , 1982 , 1225-1372 ,

    초록

    The behavior of magnesite during hot pressing is studied from 80 $0^{\circ}C$ to 110 $0^{\circ}C$ by Knoop hardness test, X-ray diffraction and electron microscopy. The growth of magnesia crystallite in magnesite is observed at 110 $0^{\circ}C$ and crystallite size is about 2 microns. It is also observed that hot pressing showes enhanced sinterability comparing to ordinary pressure-less sintering. The magnesia body with 95 per cent of theoretical density is obtained by hot pressing at relatively low temperature such as 110 $0^{\circ}C$ .

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  10. [국내논문]   카오린으로부터 $Al_2O_3$의 용출에 관한 연구   피인용횟수: 6

    백용혁 (한양대 무기재료공학과 ) , 이종근 (한양대 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.19 no.2 ,pp. 157 - 161 , 1982 , 1225-1372 ,

    초록

    The possibility of extraction of alumina from domestic Ha-dong kaolin was studied by sulfuric acid treatment. Raw kaolin was calcined at various temperature (500-110 $0^{\circ}C$ ) and calcined kaolin were treated with sulfuric acid. The tendency of extraction yield of alpha alumina have been investigated by relating reaction time, temperature, and acid concentration. After reaction, precipitates were analyzed by DTA, TGA, and identified alpha alumina by X-ray diffractometer with calcined sample at 120 $0^{\circ}C$ . The results were as follows; 1. The optimum calcination temperature was 800-86 $0^{\circ}C$ . 2. The most suitable extracting conditions of alpha alumina were 40 wt%- $H_2SO_4$ , 2-3 hours acid-treating time and 8 $0^{\circ}C$ acid-treating temperature. 3. Precipitates were composed of $(NH_4)_2SO_4$ , $Al_2SO_4(OH)_4$ 5-7 $H_2O$ and $Al(OH)_3$ .

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지

논문관련 이미지