요업학회지 = Journal of the Korean Ceramic Society 15건

  1. [국내논문]   $Al_2O_3$의 상전이 및 그에 따른 미세구조 제어에 관한 연구   피인용횟수: 1

    신상현 (한양대학교 공과대학 무기재료공학과 ) , 오창섭 (만도기계중앙연구소 ) , 최성철 (한양대학교 공과대학 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 553 - 560 , 1997 , 1225-1372 ,

    초록

    A fine $\alpha$ -Al2O3 powder was prepared by sol-gel process for membrane application. And it was carried out by adding 1.5wt% $\alpha$ -Al2O3 powders(mean size : 87 nm) as seeds to the prepared sols and by controlling the heating schedule (the heating rate and the soaking time) to prevent the microstructural change, which occured during $\theta$ -to $\alpha$ Al2O3 phase transformation. The seeded $\alpha$ -Al2O3 particles acted as the heterogeneous nucleation sites for the $\alpha$ -Al2O3 nucleation during the transformation of $\theta$ - to $\alpha$ -Al2O3 and resulted in increasing the driving force of phase transformation to activate the formation of $\alpha$ -Al2O3 phase at 82 $0^{\circ}C$ . By $\alpha$ -Al2O3 seeding and controlling of heating condition the phase transformation of $\theta$ - to $\alpha$ -Al2O3 was accomplished at low temperature and the grain growth process was depressed. Therefore, the unsupported membrane could be fabricated in $\alpha$ -Al2O3 . The average diameter of pores in the fabricated membrane was 7 nm and the porosity was 47%.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  2. [국내논문]   소결조건이 Mn-Zn Ferrites의 전자기적 물성에 미치는 효과  

    최윤호 (성균관대학교 재료공학과 ) , 신명승 (이수세라믹(주) ) , 한승기 (이수세라믹(주) ) , 한영호 (성균관대학교 재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 561 - 568 , 1997 , 1225-1372 ,

    초록

    The effects of sintering temperature and oxygen partial pressure on the electromagnetic properties of Mn-Zn ferrites were investigated. The grain increased with increasing temperature. The power loss at 100 kHz was decreased, while the power loss at 500 kHz was increased as the grain size increased with sintering temperature. Sintering with low oxygen partial pressure at 115 $0^{\circ}C$ resulted in high density and initial permeability, and decreased the power loss at 100 kHz and 500 kHz. The oxygen partial pressure lower than 10-2 atm. during heating, significantly suppressed the hysteresis loss. However, the oxygen activity did not affect the grain size of sintered cores.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  3. [국내논문]   $Pb(Mg_{1/3}Nb_{2/3})O_3-PbZrO_3$계 요업체의 전계 유기변위와 분극특성   피인용횟수: 2

    김명철 (군산대학교 공과대학 재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 569 - 576 , 1997 , 1225-1372 ,

    초록

    Electrically-induced strain and polarization studies of the (1-x)Pb(Mg1/3Nb2/3)O3-PbZrO3 crystalline solutions have been done. Dielectric constants with temperature were investigated for 0 $\leq$ x $\leq$ 0.95. With increasing PbZrO3 content the transition maxima were found to move to higher temperature region and DPT (Diffused Phase Transition) properties were decreased for x $\leq$ 0.60. Phase transition between ferroelectric states and antiferroelectric states was confirmed for 0.93 $\times$ 10-3 for 0.4

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  4. [국내논문]   반응결합에 의해 제조된 ZTA복합체의 기계적 특성   피인용횟수: 1

    장복기 (전남대학교 무기재료공학과 ) , 백용혁 (전남대학교 무기재료공학과 ) , 문종하 (전남대학교 무기재료공학과 ) , 이종호 (전남대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 577 - 582 , 1997 , 1225-1372 ,

    초록

    The mechanical properties of Al2O3-ZrO2 composites fabricated by RBAO(reaction bonded aluminium oxide) process were investigated. As the amount of ZrO2 increased the sinstered density of Al2O3-ZrO2 composites decreased slightly, but wear resistance was enhanced. Bending strength of Al2O3-ZrO2 composites increased in proportion to the amount of al in case of a fixed ZrO2 content. When the amount of Al was fixed bending strength reached its maximum value at 25 wt% ZrO2. The fracture toughness(K1c) increased with increasing content of ZrO2, but decreased with increasing Al amount. On the other hand, the fracture mode of Al2O3-ZrO2 composites was the mixed mode of inter-and transgranular fracture.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  5. [국내논문]   $Sr(Zr, Ti)O_3$ 마이크로파 유전체에 첨가된 $Mn_2O_3, Y_2O_3$ 의 영향과 Mn의 산화상태  

    정하균 (한국화학연구소 기초연구실 ) , 박도순 (한국화학연구소 기초연구실 ) , 박윤창 (성균관대학교 화학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 583 - 590 , 1997 , 1225-1372 ,

    초록

    The effects of Mn2O3 and Y2O3 additives on the microstructure and dielectric properties of Sr(Zr, Ti)O3 have been investigated. Powders with Sr(Zr1-xTix)O3(0 $\leq$ x $\leq$ 0.1) composition were prepared by the conventional solid state processing from commercial TiO2 and precipitation-processed ZrO2. The powders containing sintering additives of Mn2O3 and Y2O3 were compacted and then sintered at 1,55 $0^{\circ}C$ for 4 h to get>97% relative density. Mn2O3 suppressed the grain growth and Y2O3 enhanced the density of sintered body. The oxidation state of Mn ions were determined by a chemical wet method and EPR spectroscopy. Mn ions were present as Mn2+ and Mn4+ in SrZrO3, while as Mn3+ and Mn4+ in Ti-substituted Sr(Zr, Ti)O3. With the substitution of Ti, the lattice parameters of SrZrO3 decreased and its dielectric constant increased with remarkable decrease in Q value. The dielectric constant of Sr(Zr, Ti)O3 was in the range of 30 to 40, Q values 1,200~5,400 at 6 GHz and temperature coefficient of resonant frequency -67~100 ppm/K.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  6. [국내논문]   용융 Al의 치환반응에 의한 $Al_2O_3/Al$ 복합체의 제조   피인용횟수: 1

    정두화 (포항산업과학연구원 내화재료연구팀 ) , 김용진 ((주) 창원 기술연구소 ) , 배원태 (경상대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 591 - 600 , 1997 , 1225-1372 ,

    초록

    Al2O3/Al composites were produced by displacement reaction method, which was carried out by immersing the sintered silica preform, which was prepared from fused silica powder, in molten aluminum. Because the molten aluminum did not penetrate into the silica preform with higher than 20% of porosity when the displacement reaction was accomplished at 100 $0^{\circ}C$ for 10 hours in air atmosphere, the optimum range of sintering temperature of silica preform was from 135 $0^{\circ}C$ to 140 $0^{\circ}C$ . The microstructure of this Al2O3/Al composites showed three-dimentionally co-continuous alumina, which provides wear resistance and high stiffness, and aluminium which acts as a toughnening phase. The grain size of the alumina in composites did not change with the particle size of the silica preform. The exact shape of the preform was retained and a net-shaped composite was produced. The representative Al2O3/Al composite prepared in this study showed 3.30mg/㎤ of bulk density, 350-430 MPa of flexural strength, 7.0 MPa.m1/2 of fracture toughness, and good machinability.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  7. [국내논문]   알루미나/텅스텐 동시소성에 의한 다층 팩키지 제조시 적층조건에 따른 camber의 변화   피인용횟수: 1

    성재석 (전자부품종합기술연구소 ) , 구기덕 (전자부품종합기술연구소 ) , 윤종광 ((주) 글로텍 ) , 이상진 (일리노이 주립대학 재료공학과 ) , 박정현 (연세대학교 세라믹공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 601 - 610 , 1997 , 1225-1372 ,

    초록

    In cofiring of multilayered alumina with tungsten, the change of camber with lamination condition was experimented and the effect of sintering shrinkage of alumina and tungsten was investigated. From the exact measurement of sintering shrinkage of tungsten thick film, as lamination pressure increased, the sintering shrinkage of alumina decreased but that of tungsten thick film was not changed. So it was though that the main factor which induced the sintering shrinkage difference between ceramics and metal with lamination condition was the change of sintering shrinkage of ceramics. In case of high lamination pressure, high green sheet density, the cofired specimen showed low camber due to low shrinkage difference between alumina and tungsten and there was a linear relation between camber and shrinkage difference. It was found that this shrinkage difference could change the thickness of tungsten film and the microstructure within via hole during cofiring.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  8. [국내논문]   졸-겔법에 의한 Mullite 코팅막의 제조 및 특성에 관한 연구   피인용횟수: 1

    이용택 (경희대학교 화학공학과 재료과학기술연구소 ) , 최영우 (경희대학교 화학공학과 재료과학기술연구소 ) , 양중식 (경희대학교 화학과 재료과학기술연구소)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 611 - 619 , 1997 , 1225-1372 ,

    초록

    Optimal Mullite sol was synthesized by sol-gel process using Aluminium sec-butoxide(ASB), Tetraethoxysilane(TEOS) and then, Mullite films were dip-coated with various holding time in sol bath and heat-treated at 130 $0^{\circ}C$ above for crystallization. The thickness of coated film increased linearly with holding time in sol bath and average pore size was controllable within 20~30 $\AA$ .

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  9. [국내논문]   $0.6Pb(Ni_{1/3}Nb_{2/3})O_3-0.31PbTiO_3-0.09PbZrO_3$ 완화형 강유전체의 전계 유기 상전이 현상  

    윤만순 (주성전문대학 공학1학부 기능재료 개발 및 응용 연구실 ) , 장현명 (포항공과대학교 재료공학과 정밀 세라믹스 공정과학 연구실 ) , 정회승 (포항산업과학연구원 소재부문 기능세라믹스팀 ) , 최병철 (주성전문대학 공학1학부 기능재료 개발 및 응용 연구실)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 620 - 628 , 1997 , 1225-1372 ,

    초록

    The possibility of the existence of a field-induced micro-macrodomain switching was proposed and examined using 9 mol % PbZrO3-doped 0.6Pb(Ni1/3Nb2/3)O3-PbTiO3 (PNN-PT) systems having rhombohedral symmetry at room temperature. the thermally depoled (freshly prepard) specimens prepared from the rhombohedral side of the system exhibited a relaxor behavior for the whole range of temperature examined (for T

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  10. [국내논문]   소결조제와 열처리 분위기가 $(1-x)CaTiO_3-xLaAlO_3$ 계의 소결 및 마이크로파 유전특성에 미치는 영향   피인용횟수: 1

    이경태 (전남대학교 무기재료공학과 ) , 여동훈 (한국과학기술연구원 세라믹스부 ) , 문종하 (전남대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.6 ,pp. 629 - 635 , 1997 , 1225-1372 ,

    초록

    The effects of the annealing atmospheres(O2, N2) and sintering additives that Bi2O3 is a major composition on the microwave dielectric and sintering propertie of (1-x)CaTiO3-xLaAlO3 system were investigated. The annealing atmospheres and the increase of annealing time after sintering did not affect the relative dielectric constant( $\varepsilon$ r) and temperature coefficient of resonant frequency( $\tau$ f) of (1-x)CaTiO3-xLaAlO3 system. However, the Q.f0 values of (1-x)CaTiO3-xLaAlO3 were very sensitive to annealing atmospheres. As the annealing time increased under O2 atmosphere the Q.f0 values of (1-x)CaTiO3-xLaAlO3 enhanced untill 10 hrs in 0.3 $\leq$ x $\leq$ 0.6 region, but degraded over that time. The increasing rate of Q.f0 value increased wth increasing x. On the other hand, as the annealing time increased under N2 atmosphere the Q.f0 values were constant in x $\leq$ 0.6 region, increased gradually in x $\geq$ 0.7 region. When 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% as sintering additives were added to (Ca0.5La0.5) (Ti0.5Al0.5)O3 (x=0.5) the sintering temperature of 1 $600^{\circ}C$ was lowered to 140 $0^{\circ}C$ , and the relative dielectric constant( $\varepsilon$ r) and temperature coefficient of resonant frequency( $\tau$ f) were not nearly changed. The addition of 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% to (Ca0.5La0.5)(Ti0.5Al0.5)O3 made the Q.f0 values to be lower about 15% and 34%, respectively.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지

논문관련 이미지