요업학회지 = Journal of the Korean Ceramic Society 12건

  1. [국내논문]   화학적 기상 반응법에 의한 탄화규소 피복 흑연의 제조 (I)   피인용횟수: 1

    윤영훈 (한양대학교 무기재료공학과 ) , 최성철 (한양대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1199 - 1204 , 1997 , 1225-1372 ,

    초록

    SiC conversion layer was fabricated by the chemical vapor reaction between graphite substrate and silica powder. The CVR process was carried out in nitrogen atmosphere at 175 $0^{\circ}C$ and 185 $0^{\circ}C$ . From the reduction of silica powder with graphite substrate, the SiO vapor was created, infiltrated into the graphite substrate, then, the SiC conversion layer was formed from the vapor-solid reaction of SiO and graphite. In the XRD pattern of conversion layer, it was confirmed that 3C $\beta$ -SiC phase was created at 175 $0^{\circ}C$ and 185 $0^{\circ}C$ . Also, in the back scattered image of cross-sectional conversion layer, it was found that the conversion layer was easily formed at 185 $0^{\circ}C$ , the interface of graphite substrate and SiC layer was observed. It was though that the coke particle size and density of graphite substrate mainly affect the XRD pattern and microstructure of SiC conversion layer. In the oxidation test of 100 $0^{\circ}C$ , the SiC converted graphites exhibited good oxidation resistance compared with the unconverted graphites.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  2. [국내논문]   인산형 연료전지(PAFC)용 전해질 매트릭스의 제조방법이 전극/매트릭스 계면특성에 미치는 영향  

    윤기현 (연세대학교 세라믹공학과 ) , 최재열 (연세대학교 세라믹공학과 ) , 장재혁 (연세대학교 세라믹공학과 ) , 김창수 (한국에너지기술연구소)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1205 - 1212 , 1997 , 1225-1372 ,

    초록

    The matrices which consisted of SiC whisker, PES(polyesterasulfone) as a binder, span 80(sorbitan monooleate) as a surfactant, TPP(triphenyl phosphate) as a plasticizer and dichloromethane as a solvent, have been prepared by the various methods such as tape casting, rolling, tape cast-coating and roll-coating method. The fuel cells of single stack type using these matrices are characterized by ac impedance spectroscopy and cyclic voltammetry technique. A fuel cell using a matrix prepared by the tape cast-coating method shows the best performance of 466.34 mA/ $\textrm{cm}^2$ at 0.6V because it has the lowest polarization resistance at the interface between electrodes and a matrix due to the largest three phase contact region of gases, catalyst and electrolyte.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  3. [국내논문]   알루미나-활석계에서 알루미나의 입자 크기가 테이프 케스팅 및 소결 거동에 미치는 영향   피인용횟수: 1

    윤원균 (경북대학교 무기재료공학과 ) , 김호양 (경북대학교 무기재료공학과 ) , 이정아 (경북대학교 무기재료공학과 ) , 김정주 (경북대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1213 - 1220 , 1997 , 1225-1372 ,

    초록

    Effect of particle size of alumina and amount of talc on tape casting and densification behaviors of alumina-talc system were investigated. The pseudoplastic behaviors of slurries increased with increase in amount of talc addition and decrease in alumina particle size. In case of using coarse alumina powder, densification of specimens were accelerated with increase of sintering temperature and amount of talc addition. On the contrary, fine alumina powder retarded of rearrangement of alumina particle during liquid phase sintering due to premature densification of alumina matrix region before formation of liquid phase and then densification of specimens were suppressed with increase of sintering temperature and amount of talc addition.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  4. [국내논문]   첨가제와 소결분위기가 $SnO_2$ 요업체의 치밀화에 미치는 영향   피인용횟수: 1

    정재일 (경북대학교 무기재료공학과 ) , 김봉철 (경북대학교 무기재료공학과 ) , 장세홍 (전자부품종합기술연구소 ) , 김정주 (경북대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1221 - 1226 , 1997 , 1225-1372 ,

    초록

    The effects of sintering atmosphere and dopant addition on the behavior of densification and grain growth of SnO2 ceramics were investigated with consideration of defect chemistry. CoO and Nb2O5 were chosen as dopants, and oxygen and nitrogen were used for controlling of sintering atmospheres. With the decrease of oxygen partial pressure, densification was depressed due to evaporation of SnO2 ceramics. In the case of SnO2 sintering, the addition of CoO, which produced oxygen vacancy in SnO2 ceramics, led to acceleration of densification and grain growth. On the contrary, when Nb2O5 as a dopant producing Sn vacancy was added to SnO2 ceramics, densification and grain growth were simultaneously retarded. As results, it was conformed that diffusion of oxygen ions was rate determinant in densification and grain growth of SnO2 ceramics.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  5. [국내논문]   기판온도 및 스퍼터가스에 따른 ZnO 박막의 우선배향성, 화학조성, 물리적특성 변화  

    김병진 (인하대학교 무기재료공학과 ) , 조남희 (인하대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1227 - 1234 , 1997 , 1225-1372 ,

    초록

    ZnO thin films were prepared by rf-magnetron sputter at various conditions. Crystallinity, microstructure, chemical composition, and optical composition, and optical properties of the films were investigated as functions of substrate temperature (R. T.-50 $0^{\circ}C$ ) an sputter gas (O2/Ar=0-50%). ZnO thin films grown at 50 $0^{\circ}C$ with sputter gas of pure argon as well as at R. T. with sputter gas of a mixture of argon & oxygen(O2/Ar=2%) exhibit a strong tendency of (002) preferred orientation, compared with a considerable random orientation at the other conditions. The thin films with (002) preferred orientation has a chemical stoichiometry of Zn/O-1.01, a band gap of 3.3eV, and a packing density of 98% respectively.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  6. [국내논문]   편광 현미경을 이용한 Sodium Niobate 단결정의 분역 구조 관찰  

    정선태 (삼성전자 정보통신연구소)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1235 - 1239 , 1997 , 1225-1372 ,

    초록

    Sodium niobate single crystals were grown by high temperature solution growth with Na2O/B2O3 flux. The phase transitions and domain structures of sodium niobate were observed using transmission polarizing microscope from room temperature to $650^{\circ}C$ . There was imperfect extinction region within as-grown crystals and this area could be removed by heat treatment. The area existed within crystal till 3 $65^{\circ}C$ , in which temperature the space group of sodium niobate is changed from Pbma to Pmnm. The phase transition from Pbma to Pmnm happened abruptly with changing domain structure. At 48 $0^{\circ}C$ , 52 $0^{\circ}C$ and 572 $^{\circ}C$ , the colors and walls of domains were changed. All domains disappeared and the space group of sodium niobate was changed from P4/mbm to Pm3m at 64 $0^{\circ}C$ . When sodium niobate changed from high temperature phase to low temperature phase, the memory effect of domain structure was not observed.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  7. [국내논문]   출발상 제어에 의한 자기복합화 미세구조의 탄화규소 세라믹스 제조   피인용횟수: 1

    이종국 (조선대학교 재료공학과 ) , 강현희 (조선대학교 재료공학과 ) , 이은구 (조선대학교 재료공학과 ) , 김환 (서울대학교 무기재료공학과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1240 - 1246 , 1997 , 1225-1372 ,

    초록

    Silicon carbides with self-reinforced microstructure which hore a small grain matrix and dispersed large grains with rod-like type were prepared by the liquid-phase sintering and the control of starting phases of raw materials. The specimens with self-reinforced microstructure could be obtained from the compacts with mixed compositions of $\alpha$ -SiC and 10-50 % $\beta$ -SiC powders and by the pressureless sintering at 185 $0^{\circ}C$ for 5h. Large grains with rod or plate-like types were 4H-SiC and small grains with equi-axed type were 6H-SiC. Fracture grains with rod or plate-like types were 4h-SiC and small grains with equi-axed type were 6H-SiC. Fracture toughness of specimens with self-reinforced microstructure was increased by the crack deflection and formation of microcracking due to the existence of rod-like large grains during crack propagation.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  8. [국내논문]   요소를 이용한 활성 이트리아 분말의 합성  

    한주환 (영남대학교 금속공학 및 재료공학부)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1247 - 1253 , 1997 , 1225-1372 ,

    초록

    Sinter-active yttria powders were prepared by a solution precipitation with using a self-decomposing precipitation agent NH2CONH2(urea). The cold-pressed powders can be sintered to full density and the microstructure of grains less than 200 nm at a temperature as low as 120 $0^{\circ}C$ . The activity of the yttria powder has been controlled by varying nucleation conditions during precipitation and by minimizing formation of aggregates. The type of precursor is decisive in preparation of a sinter-active oxide powder, and urea is desirable as a precipitation agent for an active yttrium oxide powder.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  9. [국내논문]   인가 전압이 Y-TZP의 저온열화에 미치는 영향   피인용횟수: 1

    장주웅 (연세대학교 세라믹공학과 ) , 이홍림 (연세대학교 세라믹공학과 ) , 김대준 (한국과학기술연구원 세라믹스부 ) , 오남식 (한국과학기술연구원 세라믹스부 ) , 이득용 (대림전문대학 금속재료과)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1254 - 1260 , 1997 , 1225-1372 ,

    초록

    Influence of applied electric field on the low temperature degradation of 3 mol% YaO3 stabilized tetragonal zirconia polycrystals(3Y-TZP) was investigated using X-ray diffractometry of specimens aged under the dc field of 1.1 kV/mm in silicone oil both of 12 $0^{\circ}C$ -21 $0^{\circ}C$ . After the aging, the tetragonal to monoclinic phase transformation was observed only on the specimen surface of 3Y-TZP faced to the anode. This indicated that the surface was overcrowded with oxygen ions as a result of diffusion of oxygen vacancies toward the cathode-sided surface. To elucidate an influence of the applying time of the electric field on the extent of the degradation of 3Y-TZP in air, specimens were aged fore 0-2 hours under the electric field in the oil bath of 12 $0^{\circ}C$ and then subsequently aged for 3h at 22 $0^{\circ}C$ in air. The longer the specimens were aged under the field, the more extensive the transformation to the monoclinic phase was on the specimen surface faced to the cathode, probably originated from a high diffusion rate of oxygen ions due to a steep oxygen vacancy concentration gradient.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  10. [국내논문]   불산 무수석고와 플라이 애쉬를 첨가한 시멘트 페이스트의 유동성 및 응결특성   피인용횟수: 1

    노재성 (충남대학교 공과대학 정밀공업화학과 ) , 김도수 (충남대학교 공과대학 정밀공업화학과 ) , 홍성수 (호서대학교 공과대학 재료화학공학부 ) , 임계규 (호서대학교 공과대학 재료화학공학부 ) , 임헌성 (한국화학연구소)
    요업학회지 = Journal of the Korean Ceramic Society v.34 no.12 ,pp. 1261 - 1267 , 1997 , 1225-1372 ,

    초록

    Four kids of powder admixtures(A, B, C, D) based on anhydrite were manufactured by mixing at a fixed rate of II-anhydrite, fly ash and active silica as an industrial by-product. Fluidity properties of cement paste such as mini-slump, apparent viscosity with elapsed time, as well as setting time of cement pastes of these admixtures substituted up to 11wt% of cement were compared to those of cement paste(SS) substisuted by marketed high-strength powder admixture(S). Among these powder admixtures, the fluidity of cement pastes(PA, PC) substituted by A and C powder admixtures manufactured from II-anhydrite and fly ash had an excellent property than that of cement paste substituted by marketed powder admixture and also a good fluidity-retention effect with elapsed time by adding of superplasticizer. The setting time of cement paste substituted by powder admixtures based on anhydrite slightly retarded than that of cement paste substituted by marketed powder admixture.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지

논문관련 이미지