한국분말야금학회지 = Journal of Korean powder metallurgy in... 8건

  1. [국내논문]   An Overview of The Commercialisation of The Spray Forming Process  

    Leatham, Alan
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 227 - 232 , 1996 , 1225-7591 ,

    초록

    (i) The development of a metallurgical bond during the spray forming of clad products has offered the possibility of manufacturing large rolls, including those used in hot and cold strip mills. Small rolls are already being produced in Japan. (ii) Technical developments, including the use-of-multi-atomizers have resulted in the elimination of porosity from the internal bore of a sprayed tube. Bimetallic tubing can also be manufactured and the installation of a 4.5 ton tube plant in the USA should provide low operation costs. (iii) Spray forming offers a potentially low cost manufacturing route for superalloy ring/casing components in high strength superalloys. (iv) A large pilot plant has been built for the spray forming of ultra-clean superalloys for turbine disc applications. (v) Using twin-atomizing technology, special steel billets have been spray formed up to 400mm diameter with deposition yields in excess of 90%. (vi) Al/Si alloy extrusion billets with excellent dimensional tolerances are being manufactured for large scale automotive applications. Several new aluminum alloys have also been developed, including high strength, low density and low cocfficient of expansion materials. (vii) New copper alloys have been developed and pilot plants are in operation to produce these alloys once markets have become established.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  2. [국내논문]   Nanocrystalline Materials-an Overview  

    Suryanarayana, C.
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 233 - 245 , 1996 , 1225-7591 ,

    초록

    Nanocrystalline materials, with a grain size of typically

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  3. [국내논문]   급속응고기술에 의한 p-type 25% $Bi_{2}Te_{3}+75% Sb_{2}Te_{3}$ 열간압축제의 열전특성  

    김익수 (충남대학교 급속응고신소재연구소)
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 246 - 252 , 1996 , 1225-7591 ,

    초록

    $Bi_{2}Te_{3}-Sb_{2}Te_{3}$ , $Bi_{2}Te_{3}-Bi_{2}Se_{3}$ solid solutions are of great interest as materials for thermoelectric energy conversion. One of the key technologies to ensure the efficiency of thermoelectric device is to obtain chemically homogeneous solid solutions. In this work, the new process with rapid solidification followed by hot pressing was investigated to produce homogeneous thermoelectric materials. Characteristics of the materials were examined with XRD, SEM, EPMA-line scan and bending test. Property variations of the materials were investigated as a function of variables, such as excess Te quantity and hot pressing temperature. Quenched ribbons are very brittle and consisted of homogeneous $Bi_{2}Te_{3}$ , $Sb_{2}Te_{3}$ solid solutions. When the process parameters were optimized, the maximum figure of merit was 3.073 $\times$ $10^{-3}K^{-4}$ . The bending strength of the material, hot pressed at 45 $0^{\circ}C$ , was 5.87 kgf/ ${mm}^2$ .

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  4. [국내논문]   급속응고기술에 의한 n-type 90%$Bi_{2}Te_{3}+10% Bi_{2}Se_{3}$ 열간압축제의 열전특성  

    김익수 (충남대학교 급속응고신소재연구소)
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 253 - 259 , 1996 , 1225-7591 ,

    초록

    The efficiency of thermoelectric devices for different applications is known to depend on the thermoelectric effectiveness of the material which tends to grow with the increase of its chemical homogeneity. Thus an important goal for thermal devices is to obtain chemically homogeneous solid solutions. In this work, the new process with rapid solidification (melt spinning method) followed by hot pressing was investigated to produce homogeneous material. Characteristics of the material were examined with HRD, SEM, EPMA-line scan and bending test. Property variations of the materials were investigated as a function of variables, such as dopant ${CdCl}_{2}$ quantity and hot pressing temperature. Quenched ribbons are very brittle and consist of homogeneous $Bi_2Te_3$ , ${Bi}_{2}{Se}_{3}$ solid solutions. When the process parameters were optimized, the maximum figure of merit was 2.038 $\times$ $10^{-3}K^{-4}. The bending strength of the material hot pressed at 50 $0^{\circ}C$ was 8.2 kgf/ ${mm}^2$ .

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  5. [국내논문]   급속응고 Al-Si합금의 압출가공에 대한 유한요소해석  

    김의석 (충남대학교 금속공학과 및 급속응고 신소재연구소)
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 260 - 265 , 1996 , 1225-7591 ,

    초록

    Investigation on the extrusion of rapidly solidified Al-Si alloys was performed in order to develop an inexpensive production process of high strength parts. It is necessary to establish optimum process variables for the extruding condition through the experiments, because it is high cost and time consuming process. In this paper, the experimental results was compared to the finite element analysis for the extrusion of rapidly solidified Al-Si alloys. The results of this simulation helped to understand the distribution of relative density and effective stress for rapidly solidified Al-Si alloys during the extrusion process. This information is expected to assist in improving the extrusion operations of rapidly solidified Al-Si alloys.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  6. [국내논문]   농도기울기를 갖는 초경합금/철 혼합분말 성형체의 진공소결시의 미세조직 변화  

    양성철 (만도기계 중앙연구소 재료연구실)
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 266 - 270 , 1996 , 1225-7591 ,

    초록

    The microstructure evolution during sintering of a compact being composed of three layers of (WC-15%Co)/Fe powder mixture with different Fe contents has been observed. The Fe contents in the respective (WC-15%Co)/Fe layers were varied by 20%. 50%, and 90% in sequence by volume from a top layer to a bot- tom layer. The sintering temperatures and times were varied from 110 $0^{\circ}C$ to 125 $0^{\circ}C$ and from 1 h to 4 h, The compact layer was not densified below 120 $0^{\circ}C$ in 4 h. Appropriate sintering temperature and time conditions for making a multi-layered hard metal compact were determined as 125 $0^{\circ}C$ and 3 h, respectively.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  7. [국내논문]   급속응고 Al-Mg-X(X=Cr, Zr or Mn) 합금의 미세구조와 특성간의 관계  

    맹덕영 (충남대학교 금속공학과 및 급속응고신소재연구소)
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 271 - 278 , 1996 , 1225-7591 ,

    초록

    In this study, the effect of the transition elements on the microstructure and mechanical properties of rapidly solidified Al-Mg-X alloys was investigated. As a result of the rapid solidification processing, fine equiaxed grains with a mean diameter of 2 $\mu$ m were observed in these alloys. Many fine particles were found to be distributed rather homogeneously throughout the matrix with relatively large particles occasionally at grain boundaries. The ultimate tensile strengths of Al-Mg-X alloys were found to decrease rather remarkably at 150 $^{\circ}C$ without the gain of the ductility at 150 $^{\circ}C$ , which may result from segregation of $\beta$ ( $Al_{3}Mg_{2}$ ) precipitates. Fine dimples were observed on the fracture surfaces for all alloy systems and the variation of the size and shape of dimples was not observed upon alloy systems. The ductility at 530 $^{\circ}C$ was found to be ~100%, suggesting that grain boundary sliding did not contribute to ductiliy despite he grain size stabilization. The absence of superplastic behavior may be associated with low boundary misorientation in rapidly solidified Al-Mg-X alloys.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  8. [국내논문]   기계적 합금화의 $FeSi_2$계 열전재료 개발에의 응용  

    이충효 (목포대학교 재료공학과)
    한국분말야금학회지 = Journal of Korean powder metallurgy institute v.3 no.4 ,pp. 279 - 281 , 1996 , 1225-7591 ,

    초록

    In this study, the effect of the transition elements on the microstructure and mechanical properties of rapidly solidified Al-Mg-X alloys was investigated. As a result of the rapid solidification processing, fine equiaxed grains with a mean diameter of 2 $\mu$ m were observed in these alloys. Many fine particles were found to be distributed rather homogeneously throughout the matrix with relatively large particles occasionally at grain boundaries. The ultimate tensile strengths of Al-Mg-X alloys were found to decrease rather remarkably at 150 $^{\circ}C$ without the gain of the ductility at 150 $^{\circ}C$ , which may result from segregation of $\beta$ ( $Al_{3}Mg_{2}$ ) precipitates. Fine dimples were observed on the fracture surfaces for all alloy systems and the variation of the size and shape of dimples was not observed upon alloy systems. The ductility at 530 $^{\circ}C$ was found to be ~100%, suggesting that grain boundary sliding did not contribute to ductiliy despite he grain size stabilization. The absence of superplastic behavior may be associated with low boundary misorientation in rapidly solidified Al-Mg-X alloys.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지

논문관련 이미지