  1. [국내논문]   열처리조건에 따른 Bi-2212 라운드형 선재의 특성  

    이남일 (충북대학교 신소재공학과 ) , 장건익 (충북대학교 신소재공학과 ) , 오상수 (한국 전기연구원 초전도그룹 ) , 하동우 (한국 전기연구원 초전도그룹 ;) , 김상철
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 1 - 4 , 2006 , 1229-3008 ,

    초록

    The characteristics of Bi2212 round wire was systematically studied depending on different heat treatment conditions. Initial wire was drawn after routine PIT (Powder In Tube) process. The wire was divided into 3 pieces with 10 cm in length and 2.5 mm in diameter. 3 wires were pre-heat treated separately by different heat treatment schedules, heated in air and nitrogen atmosphere and centrifugally melted. Pre-heated wires were annealed at $845^{\circ}C$ for 40 hours in oxygen atmosphere. SEM results indicate that all pre-heated wires showed highly oriented microstructure. However the wire by centrifugally melted process showed higher density and better electric properties as compared with 2 other wires pre-heated in air and nitrogen atmosphere. The critical current of a centrifugally melted wire was about 18 A in 77 K.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  2. [국내논문]   저압공정을 이용한 MOD-YBCO 박막의 열처리 시간 효과  

    정국채 (한국기계연구원 신기능재료연구본부 ) , 유재무 (한국기계연구원 신기능재료연구본부 ) , 고재웅 (한국기계연구원 신기능재료연구본부 ) , 김영국 (한국기계연구원 신기능재료연구본부)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 5 - 8 , 2006 , 1229-3008 ,

    초록

    The effect of annealing time in Metal Organic Deposition(MOD) method was investigated at reduced total pressure. As the total annealing pressure was reduced, the growth rate of YBCO films increased from 0.14nm/sec at atmospheric pressure to 4.2nm/sec at 1 Torr. For the total pres sure of 700, 500, 300, 100, and 1 Torr, the optimal annealing times of 60, 40, 20, 10, 2minutes were found in our experimental conditions. When the an nealing time was short, poor crystallinity or un-reacted phase was obtained. Also, the degradation of YBCO films occurred when exposed longer to the humid ambient at the high annealing temperature. The reduced pressure was found effective to in crease the growth rate and to control the pore size of the YBCO films in MOD method. A fast growth of MOD-YBCO films was realized with high critical current density over $1MA/cm^2$ using reduced pressure annealing. Large pores, usually observed at atmospheric pressure in MOD method, disappeared and also, the number of pores was reduced.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  3. [국내논문]   Ni-W 기판 위에 동시증발법으로 제조한 SmBCO 초전도선재   피인용횟수: 1

    오상수 (한국전기연구원 초전도재료연구그룹 ) , 김호섭 (한국전기연구원 초전도재료연구그룹 ) , 하홍수 (한국전기연구원 초전도재료연구그룹 ) , 고락길 (한국전기연구원 초전도재료연구그룹 ) , 송규정 (한국전기연구원 초전도재료연구그룹 ) , 하동우 (한국전기연구원 초전도재료연구그룹 ) , 이남진 (한국전기연구원 초전도재료연구그룹 ) , 양주생 (한국전기연구원 초전도재료연구그룹 ) , 김태형 (한국과학기술원 대학원 물리학과 ) , 정예현 (경북대학교 대학원 금속공학과 ) , 염도준 (한국과학기술연구원 물리학과)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 9 - 12 , 2006 , 1229-3008 ,

    초록

    Batch type co-evaporation EDDC (Evaporation using Drum in Dual Chambers) system was recently manufactured to fabricate 100m - long SmBCO superconducting coated conductor. As a preliminary study before the fabrication of long tape. short CC samples have been fabricated using the EDDC system and their crystal texture and $I_c$ properties were investigated. $1.2 {\mu}m$ -thick SmBCO layers were deposited on $CeO_2/YSZ/CeO_2$ buffered Ni-W tapes. $I_c$ of 128A/cm-w and corresponding $J_c$ of $1.1 MA/cm^2$ at 77K in self-field were obtained for SmBCO CC tape. In-field property of SmBCO CC was confirmed to be better than that of YBCO deposited by PLD.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  4. [국내논문]   TFA-MOD 방법에 의한 YBCO 박막제조에서 nano size $Y_2O_3$ 첨가효과  

    박진아 (한국산업기술대 에너지대학원 ) , 김병주 (한국산업기술대 에너지대학원 ) , 홍계원 (한국산업기술대 에너지대학원 ) , 이희균 (한국산업기술대 신소재공학과 ) , 유재무 (한국기계연구원 신기능재료연구본부 ) , 김영국 (한국기계연구원 신기능재료연구본부)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 13 - 17 , 2006 , 1229-3008 ,

    초록

    The effect of the addition of the nano size $Y_2O_3$ powder on the microstructurte and superconducting properties of YBCO thin film deposited on LAO single crystalline substrate by TFA-MOD method was studied. Nano size $Y_2O_3$ powder was added to the stoichiometric precursor solution with a cation ratio of Y : Ba . Cu = 1 : 2 : 3 prepared using TFA as chelating agent. Precursor solutions with and without $Y_2O_3$ addition were coated on $LaAlO_3(100)$ single crystalline substrates by dip coating method. Calcination and conversion heat treatments were performed in controlled atmosphere containing moisture Current carrying capacity(Jc) of YBCO film was enhanced about 50% by $Y_2O_3$ doping and it is thought to be due to the better connectivity of YBCO grains and/or the flux pinning by the $Y_2O_3$ particles embedded in YBCO grains.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  5. [국내논문]   복합동시증착 방법을 이용한 In-situ $MgB_2$ 박막제조  

    송규정 (한국전기연구원 초전도재료연구그룹 ) , 김호섭 (한국전기연구원 초전도재료연구그룹 ) , 김태형 (한국전기연구원 초전도재료연구그룹 ) , 이영석 (한국전기연구원 초전도재료연구그룹 ) , 고락길 (한국전기연구원 초전도재료연구그룹 ) , 하홍수 (한국전기연구원 초전도재료연구그룹 ) , 하동우 (한국전기연구원 초전도재료연구그룹 ) , 오상수 (한국전기연구원 초전도재료연구그룹 ) , 문승현 (주식회사 서남 ) , 박찬 (서울대학교 재료공학부 ) , 유상임 (서울대학교 재료공학부)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 18 - 22 , 2006 , 1229-3008 ,

    초록

    We obtained in-situ $MgB_2$ thin films in an one-step process using ESSD (Evaporation Sputtering Simultaneous Deposition) method. In our approach. the Ma evaporator is designed specially Mg and B are simultaneously evaporated and sputtered, respectively, in the specially designed ESSD chamber. The background pressure was less than $1{\times}10^{-6}$ Torr. The substrate temperature was kept at 623 K. The film properties were investigated by both electrical resistivity and PPMS. As a result, typical $T_c$ of films was 11 K.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  6. [국내논문]   안정화 선재의 YBCO 초전도 접합 특성  

    김태형 (한국전기연구원 초전도재료연구그룹 ) , 오상수 (한국전기연구원 초전도재료연구그룹 ) , 하동우 (한국전기연구원 초전도재료연구그룹 ) , 김호섭 (한국전기연구원 초전도재료연구그룹 ) , 고락길 (한국전기연구원 초전도재료연구그룹 ) , 신형섭 (안동대학교 기계공학과 ) , 박경채 (경북대학교 금속신소재공학과)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 23 - 26 , 2006 , 1229-3008 ,

    초록

    For mechanical and electrical stability and environment protection. Cu and stainless steel stabilizers are laminated to a Ag layer to produce a composite neutral-axis(N-A) architecture in which the YBCO layer is centered between the oxide buffered metallic substrate and stabilizer strip lamination. This architecture allows the wire to meet operational requirements including stresses at cryogenic temperature. winding tensions as well as mechanical bending requirements including thermal and electrical stability under fault current conditions. We have experimentally studied mechanical properties of the laminated stainless steel and Cu stabilizers on YBCO coated conductors. We have laminated YBCO coated conductors by continuous dipping soldering process. We have investigated lamination interface between solder and stabilizer of the YBCO coated conductor. We evaluated bonding properties. tensile / shear bonding strength. and peeling strength laminated YBCO coated conductors.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  7. [국내논문]   Coated Conductor 에서의 복제방법의 가능성  

    임선미 (한국과학기술연구원 물리학과 ) , 유재은 (한국과학기술연구원 물리학과 ) , 염도준 (한국과학기술연구원 물리학과)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 27 - 31 , 2006 , 1229-3008 ,

    초록

    We propose a replication method to solve the problem of large percent failure in texturing processes of coated conductors. This problem is due to the individual texturing process for each coated conductor that is very long tape having no single defect spot. We tested two different methods of replication process that are based on a well-textured Ni template. First method has structure of Ni/BaO/STO/ $CeO_2$ /SmBCO/Ag. So BaO layer is dissolved in water that we can separate STO/ $CeO_2$ /SmBCO/Ag layers. In this processing, the property of STO is conserved but the superconductivity of SmBCO is deteriorated. So we can consider another method. Second method has structure of template(STO)/BaO/STO/Pt/STO. After dissolving BaO then we deposited YBCO. The result of these experiments showed the feasibility of replication.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  8. [국내논문]   $CeO_2$ 단일 완충층을 이용한 SmBCO 초전도테이프 제조  

    김태형 (한국전기연구원 초전도재료그룹 ) , 김호섭 (한국전기연구원 초전도재료그룹 ) , 하홍수 (한국전기연구원 초전도재료그룹 ) , 오상수 (한국전기연구원 초전도재료그룹 ) , 양주생 (한국전기연구원 초전도재료그룹 ) , 하동우 (한국전기연구원 초전도재료그룹 ) , 송규정 (한국전기연구원 초전도재료그룹 ) , 이남진 (한국전기연구원 초전도재료그룹 ) , 정예현 (한국과학기술연구원 물리학과 ) , 박경채 (경북대학교 금속신소재공학과)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 32 - 36 , 2006 , 1229-3008 ,

    초록

    Simplification of the buffer architecture in the fabrication of coated conductors is required because the deposition of multi-layers leads to a longer production time and a higher cost of coated conductors. In this study, a single layered buffer deposition of $CeO_2$ for low cost coated conductors has been tried using thermal evaporation technique. l00nm-thick $CeO_2$ layers deposited by thermal evaporation were found to act as a diffusion layer. $0.4{\mu}m$ -thick SmBCO superconducting layers were deposited by thermal co-evaporation on the $CeO_2$ buffered Ni-W substrate. Critical current of $55.4 A/cm^2$ was obtained for the SmBCO coated conductors.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  9. [국내논문]   MOD 공정에 의한 산화물 완충층 제조  

    김영국 (한국기계연구원 신기능재료연구본부 ) , 유재무 (한국기계연구원 신기능재료연구본부 ) , 고재웅 (한국기계연구원 신기능재료연구본부 ) , 정국채 (한국기계연구원 신기능재료연구본부)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 37 - 40 , 2006 , 1229-3008 ,

    초록

    Oxide buffer layers for YBCO coated conductors were fabricated using MOD processing and development of microstructure and texture were investigated. A $CeO_2$ buffer layers were formed on RABiTS tape. Acetate-based precursor solution was employed to synthesize the precursor solution. Subsequently, the precursor solution was stabilized and modified with triethanolamine. $CeO_2$ precursor gel film was coated and annealed in $Ar/H_2$ atmosphere at high temperature. An annealed $CeO_2$ film shows mixed orientation with high (001) texturing. It was shown that (111) texture of $CeO_2$ layers were enhanced by multiple coating. This degradation was attributed to development of microcracks in the multiply coated $CeO_2$ films. Also discussed are the synthesis and the characterization of $La_2Zr_2O_7$ (LZO) buffer layers on RABiTS tape. A biaxially textured LZO buffer layer was fabricated with MOD processing method using metal alkoxide based precursor solution. It was shown that the LZO film were epitaxially grown on RABiTS tape and crack-free & uniform surface was obtained after annealing in $Ar/H_2$ atmosphere.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지
  10. [국내논문]   초전도 HGMS법에 의한 제철공정 폐수처리  

    김태형 (한국전기연구원 초전도재료연구그룹 ) , 하동우 (한국전기연구원 초전도재료연구그룹 ) , 오상수 (한국전기연구원 초전도재료연구그룹 ) , 하홍수 (한국전기연구원 초전도재료연구그룹 ) , 박성국 (포항산업과학연구소 ) , 이상길 (포항산업과학연구소 ) , 노유미 (포항산업과학연구소)
    한국초전도·저온공학회논문지 = Superconductivity and cryogenics v.8 no.3 ,pp. 41 - 44 , 2006 , 1229-3008 ,

    초록

    This study introduced waste water treatment method by superconducting HGMS(High Gradient Magnetic Separation). HGMS treatment method is high efficient method for various waste water, we have surveyed superconducting magnetic separation technology. We fabricated the prototypes of magnetic matrix filter consisting of stainless steel mesh, which is a core component in the magnetic separation system. In our basic preliminary experiment using HGMS, it was made clear that the fine para-magnetic particles in the wasted water obtained from steelmaking process of POSCO can be separated with high efficiency.

    원문보기

    원문보기
    무료다운로드 유료다운로드

    회원님의 원문열람 권한에 따라 열람이 불가능 할 수 있으며 권한이 없는 경우 해당 사이트의 정책에 따라 회원가입 및 유료구매가 필요할 수 있습니다.이동하는 사이트에서의 모든 정보이용은 NDSL과 무관합니다.

    NDSL에서는 해당 원문을 복사서비스하고 있습니다. 아래의 원문복사신청 또는 장바구니담기를 통하여 원문복사서비스 이용이 가능합니다.

    이미지

    Fig. 1 이미지

논문관련 이미지